Abstract:To further improve the thermal shock resistance and ablation resistance of SiBCN system ceramics targeted much harsh environment, both ultra-high temperature ceramic phases and carbon fibers are expected to be incorporated simultaneously as the reinforcements. However, tough problems like difficulty in densification as well as degradation of C fibers (Cf) due to interfacial reaction usually cannot be avoided. Thus, in this study, Zr as well as chopped Cf with BN coating were introduced into SiBCN ceramics by mechanical alloying and after hot-pressing sintering to prepare C/SiBCNZr composites. The structure and phase component development have been characterized in detail by XRD, SEM, TEM and XPS etc., and mechanical properties, fracture behavior and toughening mechanisms were also investigated. Zr-B and Zr-O bonds are detected besides Si-C, N-B and N-B-C bonds when pre-alloyed ZrB2 amorphous powder was incorporated into SiBCN system by further mechanical-alloying treatment. After hot-pressing, the ultra-high temperature phases of ZrB2 and ZrN were formed as expected besides the original matrix phases of BN(C) and SiC. Excellent mechanical properties can be obtained for SiBCNZr ceramic. The BN coating on carbon fibers successfully avoids the severe fiber degradation and makes it possible for moderating strong interface bonding, which ensuring the debonding, crack deflection, fiber pulling-out and bridging during the fracture. As a result, the C/SiBCNZr composites retain good mechanical properties and fractures in a pseudoplastic fracture manner, showing better potential applications in harsh environments. Optimization of the BN coating on Cf and Zr incorporation by pre-mechanical alloying can be a good route to achieve Cf/SiBCNZr composites with a better balance between thermal shock resistance, ablation resistance and mechanical properties.

Improving mechanical properties of continuous carbon fiber-reinforced ZrB 2 -ZrSi 2 composite by addition of activated carbon

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Effects of Short Carbon Fiber on Mechanical Properties of ZrB2-SiC Ultra-high Temperature Ceramics

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Fabrication and Properties of Short Carbon Fiber-ZrB2 Ceramic Matrix Composites

Enhanced fracture properties of continuous Cf/ZrB2-based composites with polydopamine-derived carbon boundary layer

Achieving the synergy of superior damage tolerance and oxidation resistance of 2D Cf/ZrB2-SiC composites via fiber heat treatment

Effects of multilayer hydrothermal carbon interphases on mechanical properties and thermal shock resistance of CF/ZrB 2 -SiCBN

Enhanced mechanical properties and thermal shock resistance of Cf/ZrB2-SiC composite via an efficient slurry injection combined with vibration-assisted vacuum infiltration

Achieving synergy of load-carrying capability and damage tolerance in a ZrB2-SiC composite reinforced through discontinuous carbon fiber

Using flexible hydrothermal carbon-coated continuous carbon fiber to fabricate Cf/ZrB2-SiC composites by fused deposition modeling and precursor infiltration pyrolysis

Continuous carbon fiber reinforced ZrB2-SiC composites fabricated by direct ink writing combined with low-temperature hot-pressing

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Improvement in the thermal conductivities and bending strengths of graphite film/Cu composites by matrix alloying with Zr

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites

Effects of Zr and chopped C fiber on microstructure and mechanical properties of SiBCN ceramics

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Enhanced mechanical, thermal and ablation properties of carbon fiber/BPR composites modified by mica synergistic MoSi2 at 1500 °C

The effect of alloying element on the thermophysical properties of carbon fiber-graphite flakes/copper composites

Ablation behavior of ZrC-SiC-ZrB2 and ZrC-SiC inhibited carbon/carbon composites components under ultrahigh temperature conditions

Improving carbon/carbon composites mechanical and thermal properties by the co‐carbonization of pre‐oxidized carbon fiber and pitch