Abstract:Abstract Finding the optimum balance between strength and toughness, as well as acquiring reliable thermal shock resistance and oxidation resistance, has always been the most concerned topic in the discussion of ultra-high temperature ceramic composites. Herein, PyC modified 3D carbon fiber is used to reinforce ultra-high temperature ceramic (UHTC). The macroscopic block composite with large size is successfully fabricated through low temperature sintering at 1300 °C without pressure. The prepared PyC modified 3D C f /ZrC-SiC composites simultaneously possess excellent physical and chemical stability under the synergistic effect of PyC interface layer and low temperature sintering without pressure. The fracture toughness is increased in magnitude to 13.05 ± 1.72 MPa·m 1/2 accompanied by reliable flexural strength of 251 ± 27 MPa. After rapid thermal shock spanning from room temperature (RT) to 1200 °C, there are no visible surface penetrating cracks, spalling, or structural fragmentation. The maximum critical temperature difference reaches 875 °C, which is nearly three times higher than that of traditional monolithic ceramics. The haunting puzzle of intrinsic brittleness and low damage tolerance are resolved fundamentally. Under the protection of PyC interface layer, the carbon fibers around oxide layer and matrix remain structure intact after static oxidation at 1500 °C for 30 min. The oxide layer has reliable physical and chemical stability and resists the erosion from fierce oxidizing atmosphere, ensuring the excellent oxidation resistance of the composites. In a sense, the present work provides promising universality in designability and achievement of 3D carbon fiber reinforced ceramic composites.

Achieving the synergy of superior damage tolerance and oxidation resistance of 2D Cf/ZrB2-SiC composites via fiber heat treatment

Achieving synergy of load-carrying capability and damage tolerance in a ZrB2-SiC composite reinforced through discontinuous carbon fiber

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Enhanced mechanical properties and thermal shock resistance of Cf/ZrB2-SiC composite via an efficient slurry injection combined with vibration-assisted vacuum infiltration

Long‐term oxidation and ablation behavior of Cf/ZrB2–SiC composites at 1500, 2000, and 2200°C

Effect of Pyrolytic Carbon Coating on the Microstructure and Fracture Behavior of the Cf/ZrB2-SiC Composite

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

High temperature flexural strength, microstructure, phase evolution and anti-oxidation mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composite modified with TiB2 and B4C

Oxidation resistance, ablation resistance and in situ ceramization mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composites modified with Ti3SiC2

Effects of Multilayer Hydrothermal Carbon Interphases on Mechanical Properties and Thermal Shock Resistance of CF/ZrB2-SiCBN

Using PyC modified 3D carbon fiber to reinforce UHTC under low temperature sintering without pressure

Thermal Protection and Dielectric Properties of Borosilicate Coatings for SiCf/SiC Composites Under High-Temperature Oxidation

Effects of multilayer hydrothermal carbon interphases on mechanical properties and thermal shock resistance of CF/ZrB 2 -SiCBN

High-Performance Zrb2-Sic-C-F Composite Prepared by Low-Temperature Hot Pressing Using Nanosized Zrb2 Powder

Preparation and Characterization of High-Performance ZrB 2 –sic–cf Composites Sintered at 1450 °C

A universal strategy towards the fabrication of ultra-high temperature ceramic matrix composites with outstanding mechanical properties and ablation resistance

Microstructural Evolution and Performance of Carbon Fiber-Toughened ZrB2 Ceramics with SiC or ZrSi2 Additive

Design and Optimization of the Coating Thickness on Chopped Carbon Fibers and Sintering Temperature for ZrB2-SiC-C-f Composites Prepared by Hot Pressing

High-temperature Oxidation Behavior of Monolithic Zr3[Al(Si)]4C6 and Its Composite Incorporating 30vol% ZrB2-SiC: Providing a Basis for Broadening the Service Temperature

Microstructure, Mechanical Properties and Thermal Shock Resistance of ZrB 2 -Sic-c F Composite with Inhibited Degradation of Carbon Fibers