High-speed-rate direct energy deposition of Fe-based stainless steel: Process optimization, microstructural features, corrosion and wear resistance

Xiang Xu,Haifei Lu,Jinxing Qiu,Kaiyu Luo,Youyu Su,Fei Xing,Jinzhong Lu

DOI: https://doi.org/10.1016/j.jmapro.2021.12.026

IF: 5.684

2022-03-01

Journal of Manufacturing Processes

Abstract:Different types of the Fe-based stainless steel coatings were prepared by a new laser additive manufacturing technology, i.e. high-speed-rate direct energy deposition (HDED), at different deposited speeds. Subsequently, typical microstructural features, corrosion and wear behaviors were investigated. Results indicated that all the coatings were dominantly composed of ultra-fined structures with the grain size less than 2 μm. The HDEDed coating manufactured at the deposited speed of 60 m/min exhibited superior corrosive resistance with the ranking Rt (about 463.185 kΩ·cm2), which is about four time that of coating manufactured at the deposited speed of 30 m/min (about 123.910 kΩ·cm2). In addition, the lowest repassivation current density (0.16 μA/cm2) also indicates the superior secondary passivation capability. The micro-hardness of the coatings manufactured at higher deposited speeds (50 and 60 m/min) was 20% higher than that of the coatings manufactured at lower deposited speed (30 and 40 m/min). However, the wear resistance of the coatings would reach a threshold value when the deposited speed attained a certain level with the other process parameters remaining constant.

engineering, manufacturing