Microstructure and thermal properties of unalloyed tungsten deposited by Wire + Arc Additive Manufacturing

Gianrocco Marinelli,Filomeno Martina,Supriyo Ganguly,Stewart Williams,Heather Lewtas,David Hancock,Shahin Mehraban,Nicholas Lavery
DOI: https://doi.org/10.1016/j.jnucmat.2019.04.049
2019-02-15
Abstract:Tungsten is considered as one of the most promising materials for nuclear fusion reactor chamber applications. Wire + Arc Additive Manufacturing has already demonstrated the ability to deposit defect-free large-scale tungsten structures, with considerable deposition rates. In this study, the microstructure of the as-deposited and heat-treated material has been characterised; it featured mainly large elongated grains for both conditions. The heat treatment at 1273 K for 6 hours had a negligible effect on microstructure and on thermal diffusivity. Furthermore, the linear coefficient of thermal expansion was in the range of 4.5x10-6 micron m-1 K-1 to 6.8x10-6 micron m-1 K-1; the density of the deposit was as high as 99.4% of the theoretical tungsten density; the thermal diffusivity and the thermal conductivity were measured and calculated, respectively, and seen to decrease considerably in the temperature range between 300 K to 1300 K, for both testing conditions. These results showed that Wire + Arc Additive Manufacturing can be considered as a suitable technology for the production of tungsten components for the nuclear sector.
Applied Physics
What problem does this paper attempt to address?