Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Additive manufacturing and characterization of titanium wall used in nuclear application

Characterisation of additively manufactured titanium wall: Mechanical and microstructural aspects

Microstructure and Mechanical Properties of 304L Steel Fabricated by Arc Additive Manufacturing

Fabrication of stainless steel 308L wall through wire + arc additive manufacturing: Microstructure and numerical prediction of tensile test

Characterization of Wire-Arc Additively Manufactured (WAAM) of Titanium Alloy (Ti-6Al-4V) for Nanomechanical Properties

Gas Tungsten arc welding of Ti-6Al-4V sheet for pressure vessels used in aerospace application: A detailed characterization of weldment

Electron Beam Welding and Post Heat Treatment of a New Near-Beta High-Strength Ti-4Al-5Mo-5V-5Cr-1Nb Alloy

Numerical Simulation, Microstructure, and Properties of TC4 Plasma Arc Additive Manufactured Thin Wall

Effect of energy input on fatigue crack growth behavior of titanium alloy Ti6Al4V made by WAAM‐CMT

Titanium Alloy Repair with Wire-Feed Electron Beam Additive Manufacturing Technology

The State of the Art for Wire Arc Additive Manufacturing Process of Titanium Alloys for Aerospace Applications

Microstructure and thermal properties of unalloyed tungsten deposited by Wire + Arc Additive Manufacturing

A novel magnetic field assisted powder arc additive manufacturing for Ti60 titanium alloy: Method, microstructure and mechanical properties

Twin-wire plasma arc additive manufacturing of the Ti–45Al titanium aluminide: Processing, microstructures and mechanical properties

Microstructural evolution and mechanical property of Ti-6Al-4V wall deposited by continuous plasma arc additive manufacturing without post heat treatment

Wire arc additive manufacturing of commercially pure titanium bio-medical alloy

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

Influence of oxygen content in the shielding gas chamber on mechanical properties and macroscopic structure of Ti-6Al-4V during wire arc additive manufacturing

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Microstructure and mechanical properties of as-built and heat-treated Ti-6Al-4V alloy prepared by cold metal transfer additive manufacturing

Characterization of Functionally Graded Material (Stainless Steel 347/308L) Fabricated through Wire and Arc Additive Manufacturing: Microstructure and Mechanical Perspectives