Abstract:N‐type Mg3Sb2‐based material is recognized as a promising thermoelectric material. Ag is revealed as an effective dopant for the Mg3.2Sb1.5Bi0.49Te0.01 system with a different effect from Cu. A peak ZT of 1.64 at 673 K is achieved. Moreover, a 2‐pair module fabricated with MgAgSb as p‐type material, results in a high ηmax of ≈7.9% at relatively low ΔT of 277 K. The n‐type Mg3(Sb, Bi)2 compounds show great potential for wasted heat energy harvesting due to their promising thermoelectric properties. This work discovers that doping transition element Ag into the n‐type Mg3(Sb, Bi)2 can effectively optimize the power factor and suppress the lattice thermal conductivity simultaneously. Interestingly, the Ag doping has different effects compared to the isoelectronic and same group element Cu addition studied previously. A high power factor of 19.6 μW cm−1 K−2 is obtained at 673 K owing to the increased electrical conductivity. At the same time, the lattice thermal conductivity is reduced to ≈0.5 W m−1 K−1 because of enhanced phonon scattering induced by Ag atoms. These improvements lead to a peak figure of merit (ZT) of 1.64 at 673 K as well as a high average ZT of 1.27 is obtained from 323 K to 673 K. Furthermore, a thermoelectric single leg with a competitive conversion efficiency of ≈11% under a hot‐side temperature of 673 K is fabricated successfully. In addition, a 2‐pair module composed of n‐type Mg3(Sb, Bi)2 alloy and p‐type MgAgSb‐based compound demonstrates the high conversion efficiency of ≈7.9% at a temperature difference of 277 K, which will significantly upgrade the sustainable energy recycling technology.

Sintering pressure as a “scalpel” to enhance the thermoelectric performance of MgAgSb

Cost Effective Synthesis of P-Type Zn-doped MgAgSb by Planetary Ball-Milling with Enhanced Thermoelectric Properties

Revelation of Inherently High Mobility Enables Mg3Sb2 As a Sustainable Alternative to N‐bi2te3 Thermoelectrics

Extraordinary Thermoelectric Performance in MgAgSb Alloy with Ultralow Thermal Conductivity

Intrinsically high thermoelectric performance in near-room-temperature α-MgAgSb materials

Large Improvement in Thermoelectric Performance of Pressure-Tuned Mg3Sb2.

High Performance Α-Mgagsb Thermoelectric Materials for Low Temperature Power Generation

High Thermoelectric Performance of Α-Mgagsb for Power Generation

The Influence of Doping Sites on Achieving Higher Thermoelectric Performance for Nanostructured Α-Mgagsb

Understanding Anisotropy and Its Relations with Sintering Conditions on Thermoelectric Transport Properties of n-Type Mg 3 Sb 2 -Based Materials

The Microscopic Origin of Low Thermal Conductivity for Enhanced Thermoelectric Performance of Yb Doped Mgagsb

Improving Thermoelectric Performance of P-Type Ag-doped Mg2Si0.4Sn0.6 Prepared by Unique Melt Spinning Method

Realizing Cd and Ag codoping in p-type Mg3Sb2 toward high thermoelectric performance

Optimization of the thermoelectric performance of α-MgAgSb-based materials by Zn-doping

Effect of Cu Concentration on Thermoelectric Properties of Nanostructured P-Type MgAg0.97−xCuxSb0.99

Improvement of the Thermoelectric Properties of p-Type Mg 3 Sb 2 by Mg-Site Double Substitution

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Low-temperature sintering of Ag nanoparticles for high-performance thermoelectric module design

Synergy of grain size and texture effect for high-performance Mg3Sb2-based thermoelectric materials

Enhanced thermoelectric performance of Sb-doped Mg2Si0.4Sn0.6 via doping, alloying and nanoprecipitation

Enhancing the Thermoelectric Performance of n‐Type Mg3Sb2‐Based Materials via Ag Doping