Abstract:The class of NbC-Ni cermets has emerged as a promising environmentally friendly alternative to WC-Co cemented carbide tools, although some inherent properties i.e. room temperature hardness and flexural strength, of NbC-Ni cermets may require further enhancements. To enhance the properties of NbC-Ni cermets, diverse methodologies were applied, including grain inhibition and the strengthening of the cermet through the use of reinforcements. This study systematically examined the impact of TiC additions, specifically at 10% and 20%, on both the microstructure and mechanical properties of NbC-12Ni-4VC-4Mo2C cermets. NbC-12Ni cermets were fabricated via vacuum liquid phase sintering (LPS) at 1400°C and 1450°C. Enhancements by incorporating 4% VC and 4% Mo2C, followed by TiC at 10% and 20% concentrations to the NbC-Ni-4VC4Mo2C cermet were made. XRD and SEM results confirm the formation of (Nb, X, Y) C solid solution cubic FCC carbides. Significant grain refinement was evident in the cermet samples, subjected to grain inhibition. The observed grain sizes ranged from a maximum of 6.84 μm (in NbC12Ni) to a minimum of 2.154 μm (in the sample containing 20% TiC) at 1450°C. The incorporation of 20TiC at 1450°C led to a remarkable 26.5% enhancement in average hardness compared to NbC-Ni cermet, and a 4.2% improvement over the 4VC4Mo2C cermet. At 1450°C, 20TiC reinforcement led to an average fracture toughness of 9.331 MPa√m, representing a 4.56% improvement over the 4VC4Mo2C cermet. However, there was a marginal reduction in toughness compared to the NbC-Ni cermet. Moreover, the addition of TiC led to a decrease in the flexural strength of the cermets, with a maximum flexural strength of 939 N/mm2 recorded for NbC-Ni-4VC4Mo2C, representing an 11.6% increase compared to the NbC-Ni cermet.

Graded Ti(C,N)-based cermets fabricated by mechanical activation and in situ carbothermal reduction: Investigation of nitrogen sintering pressure on microstructure and mechanical performance

Experimental and thermodynamic investigation of gradient zone formation for Ti(C,N)-based cermets sintered in nitrogen atmosphere

High-quality Ti(C,N)-based cermets via solid-state nitrogen-pressure sintering: Influence of the sintering atmosphere

Relation between the nitrogen gas pressure and structure characteristics of WC–Ti(C, N)–Co graded cemented carbides

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effect of C content on the surface gradient structure of (Ti, Mo)(C, N) and Ti(C, N)-based cermets

Submicron Ti(C,N)-based cermets with improved microstructure using high-energy milled and subsequent heat-treated ultrafine Ti(C,N) powders

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

Study of Ti(C,N)-Based Cermets Fabricated by Pressureless-HIP Sintering

Study on the growth and wear characters of CVD coating deposited on Ti(C, N)-based cermets with adding different C/N ratios of Ti(C, N) powders

High pressure in-situ synthesis and physical properties of Cr3C2-Ni cermets

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Microstructure, Interface Characteristics and Mechanical Properties of Ti(C,N)-based Cermets with a Cellular Structure

Effect of the nitrogen multi-sources on the microstructure and hardness of the graded surface layer in WC–Co–Cubic cemented carbides

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

The production of in situ (Mo,Ti)(C,N)-based cermets without a core/rim structure by reaction hot pressing: Formation mechanism and mechanical properties

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Enhanced Densification of Ultrafine Ti(C, N)-based Cermets Based on Grain-Growth Induced Liquid-Phase Pore Filling Mechanism

Effect of diamond addition on microstructure and mechanical properties of Ti(C,N)-based cermets

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets