Abstract:In order to realize the utilization of coal-fired solid waste and captured carbon dioxide, the effects of ratio of solid waste, mineralized curing pressure and mineralized curing temperature on the compressive strength and carbon fixation rate of aerated concrete were studied, with the coal-based waste, coal ash and desulfurization gypsum as the main raw materials and slag as the supplementary cementitious material. The crystal phase structure and micro morphology under different mineralized curing conditions were analyzed by XRD and SEM, and the effect of different mineralized curing conditions on the pore structure of aerated concrete was studied by MIP. The experimental results show that the appropriate residual water/slag ratio is helpful to improve the CO 2 fixation rate and early compressive strength of aerated concrete. When the CO 2 curing pressure increases from 0.05 MPa to 1.00 MPa, the carbon fixation rate increases by 24.8%, and the compressive strength increases first and then decreases. When the curing pressure is 0.1 MPa, the maximum compressive strength is reached. With the CO 2 curing temperature rising from 25 ℃ to 105 ℃, the carbon fixation rate and compressive strength increases first and then decreases. The carbon fixation rate reaches maximum of 7.21% at 45 ℃, and the compressive strength reaches maximum of 3.53 MPa at 65 ℃. According to analysis of XRD and SEM, the major mineralized products are CaCO 3 , which mainly exist in the form of calcite and vaterite. Higher curing pressure（≥0.2 MPa） is likely to cause micro-cracks at the product interface. With the increase of curing temperature, the mineralized products and hydrated products appear simultaneously. According to MIP analysis, the influence of mineralized curing on the pores of aerated concrete can be divided into two aspects: on the one hand, CaCO 3 and other products with small particle size can fill the pores of 10-50 nm, on the other hand, reaction heat of mineralization and volumetric expansion of products can cause the increase of 30-60 μm pores. The microstructure can be optimized by increasing the curing temperature, which can make the distribution of pores more uniform.

High-performance aerated concrete building material utilizing barium slag and preparation method thereof

Carbonation Curing of Industrial Solid Waste‐based Aerated Concretes

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Coal fired furnace slag autoclaved aerated concrete building block and preparation method of coal fired furnace slag autoclaved aerated concrete building block

Utilization of Carbide Slag in Autoclaved Aerated Concrete Preparation

Experimental Research on Aerated Concrete Preparation with Low-Silicon Tailings of Copper Mine

Leaching assessment of aerated concrete made of recycled shale gas drilling cuttings: Particular pollutants, physical performance and environmental characterization

Experimental Study Based on Box–Behnken Design and Response Surface Methodology for Optimization Proportioning of Activated Lithium Slag Composite Cement-Based Cementitious Materials

Steel Slag Accelerated Carbonation Curing for High-Carbonation Precast Concrete Development

Study on Preparation and Performance of Brick-concrete Recycled Sand Powder Autoclaved Aerated Concrete

Utilizing Ceramic Waste for Autoclaved Aerated Concrete

Preparation of Autoclaved Aerated Concrete from Construction Waste

Using hazardous barium slag as a novel admixture for alkali activated slag cement

Study on formulation of aerated concrete by CO2 mineralization using coal ash

Utilization of barium slag to improve chloride-binding ability of cement-based material

Preparation of slag-based foam concrete and its carbon dioxide sequestration performance

Preparation of Cementitious Materials from Mechanochemically Modified Copper Smelting Slag Compounded with High-Aluminum Fly Ash

Research on the methods for improving the compressive strength of solid waste-based high-strength autoclaved aerated concrete

Development of Alkali-Activated Porous Concrete Composition from Slag Waste

Modification of ultrafine blast furnace slag with steel slag as a novel high-quality mineral admixture to prepare high-strength concrete

Modification mechanism of flue gas desulfurization gypsum on fly ash and ground granulated blast-furnace slag alkali-activated materials: Promoting green cementitious material