Abstract:Commonly used alkali activation precursors such as blast furnace slag and fly ash will soon become less available due to resource competition, and may cease to be produced in certain regions. This limitation in future supply is a main driving force for the investigation of alternative precursor sources, such as non-blast furnace slags and non-ferrous slags, to produce alkali-activated binders. The current study investigates the incorporation of copper slag (CS) and stainless steel slag resulting from electric arc furnace operations (EAFSS) as partial replacements for ground granulated blast furnace slag (GGBFS) in producing alkali-activated materials (AAMs), at paste level. Five binary alkali-activated mixtures with different replacement levels of GGBFS with CS, and three ternary mixtures with both CS and EAFSS as partial and total replacements for GGBFS, are activated by a sodium silicate solution. Replacing GGBFS with CS and EAFSS retards the reaction kinetics, resulting in improved fresh-state properties of the investigated AAMs, better retention of workability and longer setting times. The reaction of alkali-activated 100% CS shows minimal initial exothermic activity until 3.5 h, when a single intense peak appears, representing delayed dissolution and subsequent polycondensation. X-ray diffraction (XRD) data indicate that the main crystalline phases of CS and EAFSS are stable in these alkaline systems; it is the glassy components that react. The use of CS and EAFSS in blended AAMs causes a minor increase in porosity of ~ 1–3% with respect to GGBFS only, and a small reduction in compressive and flexural strengths, although these reach 80 MPa and 8 MPa, respectively, after 28 days, even at a replacement level over 65 wt. %. Conversely, the 100% CS mixture exhibits a one-day compressive strength of 23 MPa, with a negligible increase thereafter. This result agrees with both FTIR and SEM analysis which highlight only minor changes in binder development after two days. It is believed that the unusual behaviour of CS in the investigated mixtures is related to the low availability of calcium in this precursor material.

Using hazardous barium slag as a novel admixture for alkali activated slag cement

Preparation of Coal Gasification Coarse Slag-Based Alkaline Activator and Its Activation Mechanism in Alkali-Activated Slag

Utilization of barium slag to improve chloride-binding ability of cement-based material

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Admixture Effects on the Rheological/Mechanical Behavior and Micro-Structure Evolution of Alkali-Activated Slag Backfills

Synergistic positive effects of nano barium silicate on the hydration rate and phase composition of alkali-activated slag

Evaluation of copper slag and stainless steel slag as replacements for blast furnace slag in binary and ternary alkali-activated cements

Research on rheology performance and sealing effect of alkali-activated GGBS paste used for tunnel leakage plugging

A Novel Alkali-Slag Cemented Tailings Backfill: Recycling of Soda Residue and Calcium Carbide Slag

Synergistic use of electrolytic manganese residue and barium slag to prepare belite- sulphoaluminate cement study

Utilization of carbide slag-granulated blast furnace slag system by wet grinding as low carbon cementitious materials

Comparison of Mechanical Properties and Microstructure of GGBS-based Cementitious Materials Activated by Different Combined Alkaline Wastes

Application of molten iron desulfurization slag to replace steel slag as an alkaline component in solid waste-based cementitious materials

Study on the properties of alkali-activated phosphorus slag mortar mixed with granulated blast furnace slag/fly ash

Effect of Alkali Content on the High-Temperature Behavior of Alkali-Activated Slag Paste Containing MSWI Bottom Ash

The Solidification of Lead-Zinc Smelting Slag through Bentonite Supported Alkali-Activated Slag Cementitious Material

Use of Alkali-Activated Slag as an Environment-Friendly Agent for High-Performance Stabilized Soil

Effect of carbide slag and steel slag as alkali activators on the key properties of carbide slag-steel slag-slag-phosphogypsum composite cementitious materials

Investigation on the basic performance of the sustainable alkali-activated slag blended with sulphidic copper tailings

Preparation and Characterization of Low-Carbon Cementitious Materials Based on Soda-Residue-Activated Ground Granulated Blast-Furnace Slag: A Case Study on Cemented Paste Backfills

Recycling of steel slag as an alkali activator for blast furnace slag: geopolymer preparation and its application in composite cement