Abstract:Plasma nitriding is widely used in various industrial applications to improve surface hardness and wear properties. Especially for tool steels, it is also used to improve the support and adhesion of diamond-like carbon (DLC) coatings. The properties of the nitrided zone produced by plasma nitriding are influenced by the applied process parameter, in particular temperature and time. However, for high-alloy tool steels, a deeper understanding of the underlying diffusion processes of the nitrogen and the interaction with the existing microstructure, as well as the effects on the case depth is still lacking. Therefore, in this study, specimens of high-alloy tool steel X153CrMoV12 were plasma nitrided at varying temperatures (480 °C, 520 °C, 560 °C) and treatment times (2 h, 4 h, 16 h). The resulting nitrided zones were investigated by optical and scanning electron microscopy (OM and SEM), depth-dependent glow discharge optical emission spectroscopy (GDOES), X-ray diffraction (XRD), and hardness measurements to characterize their microstructure, chemical composition, and hardness depending on the process parameters. The distribution of carbides (M7C3), e.g., chromium carbides, affects the diffusion of the nitrogen and the layer growth. An increase of temperature and duration leads to an increased layer thickness. The composition of the compound layer is, e.g., influenced by the process parameters: ε nitrides (Fe2–3N) occurred preferentially at lower temperatures, while γ′ nitrides (Fe4N) appeared mostly at higher temperatures. In order to investigate the influence of the carbides of the high-alloy tool steel on the nitriding process, a new methodology was developed by means of finite element analysis (FE), which makes it possible to analyze this influence on the development of the nitrogen concentration profile. This methodology makes it possible for the first time to map the heterogeneous nitrogen evolution and distribution.

The Microstructure of Tool Steel after Low Temperature Ion Nitriding

Nanosized precipitates in H13 tool steel low temperature plasma nitriding

Tool steel ion beam assisted nitrocarburization

Evolution of Microstructure and Hardness of the Nitrided Zone during Plasma Nitriding of High-Alloy Tool Steel

Tribological Studies of Plasma Source Ion Nitrided Low Alloy Tool Steel

Study of the effect of ion nitriding regimes on the structure and hardness of steel

Microstructure–Wear Resistance Relationship of Nitrogen-Containing High-Speed Tool Steel, AISIM41: Non-equilibrium Solidification

In situ photoemission electron spectroscopy study of nitrogen ion implanted AISI-H13 steel

Microstructural characterization of plasma nitrided austenitic stainless steel

Microstructure and Characterization of High Hardness Produced in High-Nitrogen Austenite Intermediate Temperature Transformation

Characterization of Vein-Like Structures Formed in Nitrided Layers During Plasma Nitriding of 8cr4mo4v Steel

Formation of A Nanostructured Crn Layer on Nitrided Tool Steel by Low-Temperature Chromizing

Micro-/Meso-Structure Control of Multi-Hostmetal Alloys by Massive Nitrogen Supersaturation

Effects of Initial Microstructure on the Low-Temperature Plasma Nitriding of Ferritic Stainless Steel

Ion nitriding of martensitic and austenitic steels after SPD at different temperatures

Low-temperature plasma nitriding of martensitic stainless steel

Microstructure in Implanted Layer of 1cr18ni9 Steel Implanted at Elevated Temperature

Microstructure evolution and nanohardness of nanostructured TiAlN coating under N+ ion irradiation

Effect of High-Energy Shot-Peening on H13 Tool Steel Ion-Nitriding

Effect of ion nitriding by glow discharge on the physical and mechanical properties of the plastically deformed tool steel R6M5

Nitrogen Ion Implantation on the Mechanical Properties of Aisi 420 Martensitic Stainless Steel