Abstract:The nucleation, crystallization, and growth mechanisms of MnFe2O4, CoFe2O4, NiFe2O4, and ZnFe2O4 nanocrystallites prepared from coprecipitated transition metal (TM) hydroxide precursors treated at sub-, near-, and supercritical hydrothermal conditions have been studied by in situ X-ray total scattering (TS) with pair distribution function (PDF) analysis, and in situ synchrotron powder X-ray diffraction (PXRD) with Rietveld analysis. The in situ TS experiments were carried out on 0.6 M TM hydroxide precursors prepared from aqueous metal chloride solutions using 24.5% NH4OH as the precipitating base. The PDF analysis reveals equivalent nucleation processes for the four spinel ferrite compounds under the studied hydrothermal conditions, where the TMs form edge-sharing octahedrally coordinated hydroxide units (monomers/dimers and in some cases trimers) in the aqueous precursor, which upon hydrothermal treatment nucleate through linking by tetrahedrally coordinated TMs. The in situ PXRD experiments were carried out on 1.2 M TM hydroxide precursors prepared from aqueous metal nitrate solutions using 16 M NaOH as the precipitating base. The crystallization and growth of the nanocrystallites were found to progress via different processes depending on the specific TMs and synthesis temperatures. The PXRD data show that MnFe2O4 and CoFe2O4 nanocrystallites rapidly grow (typically <1 min) to equilibrium sizes of 20-25 nm and 10-12 nm, respectively, regardless of applied temperature in the 170-420 C range, indicating limited possibility of targeted size control. However, varying the reaction time (0-30 min) and temperature (150-400 C) allows different sizes to be obtained for NiFe2O4 (3-30 nm) and ZnFe2O4 (3-12 nm) nanocrystallites.

Development of various methods for PrF3 nanoparticles synthesis

Microwave-assisted hydrothermal synthesis and characterizations of PrF3 hollow nanoparticles

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Synthesis of PrF3 hollow nanoparticles and praseodymium hydroxide nanorods by microwave irradiation

Hydrothermal Synthesis and Characterization of Rare Earth Compound Nanoparticles and Nanorods

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of REF3 (re=nd, Tb) Nanoparticles Via a Solvent Extraction Route

Synthesis of LaF3: Yb3+,Ln3+nanoparticles with Improved Upconversion Luminescence

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Direct hydrothermal synthesis of single-crystalline triangular Fe3O4 nanoprisms

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method

Large-scale solution synthesis of alpha-AlF3 center dot 3H(2)O nanorods under low supersaturation conditions and their conversion to porous beta-AlF3 nanorods

Hydrothermal Synthesis of Magnetic Fe3O4 Hexagonal and Single Crystal Nanorods

Hydrothermal synthesis of monodisperse α-Fe2O3 nanocubes

Reaction Study Of Alpha-Phase Nayf4:Yb,Er Generation Via A Tubular Microreactor: Discovery Of An Efficient Synthesis Strategy

Radiation-chemical synthesis and characterization of ferrihydrite from iron (III) nitrate

Synthesis and characterization of MgF2 and KMgF3 nanorods

The Chemistry of Spinel Ferrite Nanoparticle Nucleation, Crystallization, and Growth

Preparation of Nanocrystalline Fe3O4 by Γ-Ray Radiation

Synthesis of Fe<sub>3</sub>O<sub>4</sub> Magnetic Nanoparticles in a Helical Microreactor

Synthesis and Characterization of Praseodymium Hydroxide Nanorods by a Hydrothermal Process