Abstract:LaF3 : Tba3+, Ce3+ nanocrystals were prepared with hydrothermal method with the help of cetyltrimethyl ammonium bromide (CTAB). The effects of pH values of the solution, Ce3+/Tb+ ratio value and reaction time on the luminescent properties were investigated. XRD analysis shows that the as-prepared samples possess hexagonal phase and their main diffraction peaks of samples are similar to the standard card (JCPDS 32-0483). Compared with pure LaF3, the main diffraction peaks of the doped samples have a slight shift, showing existing isomorphous substitution between La3+ and the doped rare earth ions in parent lattice of LaF3. It is found from TEM results that the as-prepared samples have good crystallinity and their average grain sizes change in the range of 20-50 nm. The excitation spectra indicate that the stronger excitation spectrum peaks exist at 250 nm, which is assigned to the transition of 4f --> 5d from Ce3+. When activated at 250 nm, all LaF3 : Tb3+, Ce3+ nanocrystals possess weak blue emission at 490 nm (electric dipole transition, 5D4 --> 7F6) and good green emission at 543 nm (magnetic dipole transition, 5D4 -->7F5). As the Ce3+/Tb+ ratio increases, the fluorescence intensities increase at first and then weaken, and reach the strongest green emission at n(Ce)3+ /n(Tb)3+ = 4. The pH values have some influence on the colors and intensities of the LaF3 : Tb3+, Ce3+ nanocrystals. The sample prepared at pH 9 presents the best color, while the one at pH 7 exhibits the strongest green emission. Besides, increasing reaction time is helpful to improve color purity of sample and enhance its green emission.

Hydrothermal Synthesis and Characterization of Rare Earth Compound Nanoparticles and Nanorods

Low-temperature chemical solution synthesis of dendrite-like La(OH) 3 nanostructures and their thermal conversion to La 2 O 3 nanostructures

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Synthesis of LaF3: Yb3+,Ln3+nanoparticles with Improved Upconversion Luminescence

Synthesis and Characterization of Praseodymium Hydroxide Nanorods by a Hydrothermal Process

Microwave-assisted hydrothermal synthesis and characterizations of PrF3 hollow nanoparticles

Hydrothermal Synthesis Of Rare-Earth Fluoride Nanocrystals

Reductive Hydrothermal Synthesis of La(OH) 3 :Tb 3+ Nanorods As a New Green Emitting Phosphor

Synthesis of PrF3 hollow nanoparticles and praseodymium hydroxide nanorods by microwave irradiation

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Controlled synthesis of light rare-earth hydroxide nanorods via a simple solution route

Synthesis and Characterization of Lanthanum Hydroxide by Hydrothermal Method

Facile synthesis of water-soluble LaF3∶ Ln3+ nanocrystals

Hydrothermal Synthesis of Rare Earth (Tb, Y) Hydroxide and Oxide Nanotubes

Synthesis of Lanthanum Hydroxide Nanorods in the Media of Reverse Microemulsions

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

[Study on the Hydrothermal Synthesis and Fluorescence of LaF3 : Tb3+, Ce3+ Nanocrystals]

Microwave-Assisted Synthesis of Praseodymium Hydroxide Nanorods and Thermal Conversion to Oxide Nanorod

Selective synthesis of LaF3 and NaLaF4 nanocrystals via lanthanide ion doping

Amine-Assisted Synthesis and Characterization of Lanthanide Hydroxide Nanorods and Derived Oxides