Abstract:The failure of composite laminates under cyclic fatigue loads is complex, as multiple failure mechanisms are in play at different scales and interact with each other. Predicting the remaining fatigue life as well as the residual capacities of a composite laminate or component is crucial, particularly for safety-critical applications. A progressive fatigue model is proposed to describe the catastrophic failure of open-hole laminates under tensile cyclic fatigue. To represent both intra-laminar and inter-laminar damage, a combination of a continuum damage mechanics model (CDM) and a discrete cohesive zone model (CZM) is implemented in the finite element (FE) software Abaqus. The CDM combines fibre- and matrix-dominated S-N curves with the Palmgren–Miner accumulation rule and Hashin’s residual strength to form a fatigue failure criterion differentiating between fibre failure (FF) and matrix failure (MF). The CZM implemented in this work is the CF20 model proposed by NASA. Fatigue cycling is simulated using an external cycle-jump scheme, where the stiffness degradation is conducted between the FE simulations outside of the implicit solver [90/0] s. Glass fibre reinforced polymer (GFRP) open-hole specimens were tested in tensile cyclic fatigue at a load ratio of 0.1. The experiments were reproduced numerically and the results compared. After calibration of a set of parameters based on one load level, the model was able to reproduce the experimental S-N curve very well, predicting a slope of −0.10, while the experimental value was −0.11. The failure sequence of the laminate was also successfully reproduced. The growth of the split from the hole, and its interaction with inter-laminar delamination, was successfully captured. The proposed approach was able to describe the fatigue failure of an open-hole laminate with a minimal set of material inputs using a simplified fatigue damage model while avoiding convergence issues.

Cyclic damage quantification in composite materials using discrete damage mechanics

A New Approach to Low-Cycle Fatigue Damage Based on Exhaustion of Static Toughness and Dissipation of Cyclic Plastic Strain Energy During Fatigue

A New Approach for Studying Fatigue Damage

Evaluation and Modeling of the Fatigue Damage Behavior of Polymer Composites at Reversed Cyclic Loading

A Continuum Damage and Discrete Crack Module for Fatigue Damage Prediction of Laminated Composite Structures

On the experimental determination and prediction of damage evolution in composites via cyclic testing

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

A Fatigue Model to Predict Interlaminar Damage of FRP Composite Laminates Subjected to Mode I Load

On Cyclic-Fatigue Crack Growth in Carbon-Fibre-Reinforced Epoxy–Polymer Composites

Fatigue-driven failure criterion for progressive damage modelling and fatigue life prediction of composite structures

A numerical framework for simulating progressive failure in composite laminates under high-cycle fatigue loading

Modeling of progressive high-cycle fatigue in composite laminates accounting for local stress ratios

A damage model for matrix cracks in composite laminates under fatigue loading based on continuum damage mechanics

A novel damage characterization approach for laminated composites in the absence of material and structural information

A continuum damage mechanics model for fatigue degradation and failure of short fiber reinforced composites

The Discontinuous Strain Method: accurately representing fatigue and failure

Fatigue delamination damage analysis in composite materials through a rule of mixtures approach

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Fatigue accumulated damage in notched quasi-isotropic composites under high-temperature conditions: A discussion on the influence of matrix nature on the stress energy release rate

Fatigue Damage and Degradation in Random Short-Fiber SMC Composite

Adjunctive Damage Model to Describe the Interaction of Different Defect Types in Textile Composites on the Strain-Rate-Dependent Material Behaviour