Abstract:In this work, a recently proposed high-cycle fatigue cohesive zone model, which covers crack initiation and propagation with limited input parameters, is embedded in a robust and efficient numerical framework for simulating progressive failure in composite laminates under fatigue loading. The fatigue cohesive zone model is enhanced with an implicit time integration scheme of the fatigue damage variable which allows for larger cycle increments and more efficient analyses. The method is combined with an adaptive strategy for determining the cycle increment based on global convergence rates. Moreover, a consistent material tangent stiffness matrix has been derived by fully linearizing the underlying mixed-mode quasi-static model and the fatigue damage update. The enhanced fatigue cohesive zone model is used to describe matrix cracking and delamination in laminates. In order to allow for matrix cracks to initiate at arbitrary locations and to avoid complex and costly mesh generation, the phantom node version of the eXtended finite element method (XFEM) is employed. For the insertion of new crack segments, an XFEM fatigue crack insertion criterion is presented, which is consistent with the fatigue cohesive zone formulation. It is shown with numerical examples that the improved fatigue damage update enhances the accuracy, efficiency and robustness of the numerical simulations significantly. The numerical framework is applied to the simulation of progressive fatigue failure in an open-hole [$\pm$45]-laminate. It is demonstrated that the numerical model is capable of accurately and efficiently simulating the complete failure process from distributed damage to localized failure.

What problem does this paper attempt to address?

### Problems Addressed by the Paper This paper aims to address the issue of progressive failure simulation of composite laminates under high-cycle fatigue loading. Specifically: 1. **Fatigue Cohesive Zone Model**: - A new high-cycle fatigue Cohesive Zone Model (CZM) is proposed, which can describe the initiation and propagation of cracks with fewer input parameters. - The model is enhanced with an implicit time integration scheme, allowing for larger cycle increments, thereby improving analysis efficiency. 2. **Numerical Framework**: - The aforementioned fatigue CZM is embedded into a robust and efficient numerical framework to simulate the progressive failure process of composite laminates under fatigue loading. - An adaptive strategy is combined to determine the cycle increments, optimizing computational efficiency based on global convergence rates. 3. **Material Tangent Stiffness Matrix**: - A fully consistent material tangent stiffness matrix is derived through complete linearization of the underlying mixed-mode quasi-static model and fatigue damage updates. 4. **Application of Extended Finite Element Method (XFEM)**: - The Phantom Node Version of XFEM is used, allowing matrix cracks to occur at arbitrary locations, thus avoiding complex mesh generation. - An XFEM fatigue crack insertion criterion consistent with the fatigue CZM formulation is proposed. 5. **Accuracy and Efficiency**: - Numerical examples demonstrate that the improved fatigue damage updates significantly enhance the accuracy, efficiency, and robustness of numerical simulations. - The numerical framework is applied to simulate the progressive failure process of an open-hole [±45] laminate under fatigue loading, showcasing the model's ability to accurately and efficiently simulate the complete process from initial damage to local failure. In summary, this paper is dedicated to developing an efficient numerical tool for predicting the progressive failure behavior of composite laminates under high-cycle fatigue conditions, with a particular focus on the simulation of matrix cracks and interfacial delamination.

A numerical framework for simulating progressive failure in composite laminates under high-cycle fatigue loading

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Modeling of progressive high-cycle fatigue in composite laminates accounting for local stress ratios

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension

A Phase-Field Framework for Modeling Multiple Cohesive Fracture Behaviors in Laminated Composite Materials

A continuum damage mechanics model for fatigue degradation and failure of short fiber reinforced composites

A novel implementation of the cohesive zone model for the fatigue propagation of delamination in composites using a sequential static fatigue algorithm

A Continuum Damage and Discrete Crack Module for Fatigue Damage Prediction of Laminated Composite Structures

A phase-field fracture model for fatigue behavior in fiber-reinforced composites

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

High-Fidelity Analyses of Composites at Various Length Scales with Discrete Damage Representations

Evaluation and Modeling of the Fatigue Damage Behavior of Polymer Composites at Reversed Cyclic Loading

Fatigue life prediction of hybrid carbon-flax-epoxy laminates using progressive failure analysis and cohesive zone model

Progressive Failure Analysis of Composite Laminates Subjected to Transverse Loading with Augmented Finite Element Method

Progressive fracture analysis of the open-hole composite laminates: experiment and simulation

Numerical Simulation Of Composites At Various Length Scales: Where Are The Limits

Progressive Failure Analysis of Carbon Fiber/epoxy Composite Laminates Using Continuum Damage Mechanics

A damage model for matrix cracks in composite laminates under fatigue loading based on continuum damage mechanics

Delamination Buckling and Crack Propagation Simulations in Fiber-Metal Laminates Using xFEM and Cohesive Elements

A Fatigue Model to Predict Interlaminar Damage of FRP Composite Laminates Subjected to Mode I Load