A damage model for matrix cracks in composite laminates under fatigue loading based on continuum damage mechanics

Wenxuan Qi,Jie Huang,Weixing Yao,Haojie Shen
DOI: https://doi.org/10.1016/j.ijfatigue.2024.108315
IF: 5.489
2024-04-03
International Journal of Fatigue
Abstract:A damage model for transverse matrix cracks in composite laminates under fatigue loading was presented in this paper. The model was prosed based on the theory of continuum damage mechanics (CDM) at macro level and could capture the 'edge effect' of matrix cracks in composite laminate under fatigue loading. To obtain the constitutive equation of UD lamina containing transverse matrix cracks, a polynomial Gibbs free energy function was derived, and a macro damage parameter was introduced to characterize the influence of matrix cracks on multidirectional stiffness properties of UD composite. To predict the initiation and evolution of matrix cracks, a previously deduced initial crack initiation life function and a Paris-like equation in terms of damage driving force were employed, respectively. Prediction results of two cross-ply laminates under fatigue loading with different stress levels were compared to the experimental results and prediction results obtained from previously proposed model. The comparison results indicate the presented model is more effective and reliable in predicting the initiation and evolution of matrix cracks and the corresponding stiffness degradation in composite laminates under fatigue loading.
materials science, multidisciplinary,engineering, mechanical
What problem does this paper attempt to address?