Abstract:This paper describes the experimental parameters involved in the femtosecond laser micromachining of biodegradable poly(L-lactide) which is frequently used in biomedical applications such as vascular stents or scaffolds. We investigated the influence of laser pulse energy, scanning strategy and number of overscans on the laser cutting throughput. The process parameters that enable reducing a heat affected zone were determined. As a result, the optimal scanning strategy was determined in order to obtain high aspect ratio trenches in a 380μm thick biodegradable polymer sheet. Over the last decade we have observed the increasing involvement of femtosecond lasers for manufacturing biomedical devices made of biodegradable polymers. A small beam diameter and short pulse duration enable forming complex, submillimeter geometrical shapes in polymers such as vascular stents which cannot be manufactured using traditional techniques e.g. injection moulding or mechanical processing. The shortening of pulse duration below electron cooling time enables reduction of thermal and mechanical damage to the surrounding material. Furthermore, extremely high power density causes multiphoton absorption that allows for processing wide-bandgap dielectrics. Together with high pulse energy in the range of tens of microjoules attainable in modern industrial constructions, femtosecond lasers appear as a perfect tool for efficient machining of polymers. There are, however, several limitations regarding the use of femtosecond lasers for processing heat sensitive biodegradable polymers. As it was reported previously, laser micromachining with ultrashort pulse lasers can result in thermal load affecting the surrounding material causing its melting, crack formation [1-2] or crystallisation [3]. Nevertheless, heat accumulation appears mainly for a high repetition rate, high pulse energy and multiple scanning cycles. Depending on the relation between laser wavelength, fluence, repetition frequency and pulse overlapping, the process can be designed to be a-thermal [2]. In order to preserve a relatively high process throughput one can apply different strategies such as decreasing pulse overlapping [4] or * E-mail: bogusz.stepak@pwr.edu.pl using gas assist [2]. Another issue affecting the processing speed is the reflection and scattering of incident light in a V-shaped groove causing a decrease of the ablation rate with an increasing number of over-scans [5]. This article presents the results of the cutting process optimisation of medical grade poly(L-lactide) (PLLA – RESOMER® L 210 S, Evonik Biomaterials). PLLA is a semicrystalline aliphatic polyester which is transparent in a wide optical window beginning from 250nm up to near infrared. The thickness of an amorphous polymer sheet prepared using a hydraulic press was 380±10μm. The experiments were performed using s laser from Active Fiber Systems Jena with the pulse duration τ=450fs, wavelength λ=515nm and fixed pulse repetition frequency 10kHz. The focal length of the lens was 163mm and the beam diameter in the focal plane was 25μm. The laser cutting trials were performed in ambient air using a test pattern that consists of six grooves with a length of 1mm and a different width (Fig. 1). The grooves were produced by bidirectional scanning in the y direction each with the hatching distance10μm.

High-quality cutting of polypropylene (PP) film by UV nanosecond laser based on thermal ablation

Process and mechanism of cutting thermoplastic polyurethane (TPU) film by nanosecond ultraviolet laser

Cutting of polyethylene terephthalate (PET) film by 355 nm nanosecond laser

Precision cutting of polyvinyl chloride film by ultraviolet nanosecond laser

Temperature Field-Assisted Ultraviolet Nanosecond Pulse Laser Processing of Polyethylene Terephthalate (PET) Film

High-quality cutting polarizing film (POL) by 355 nm nanosecond laser ablation

High-speed pump-probe imaging of ultrashort pulsed laser cutting of polymers

Study on the ultraviolet nanosecond laser ablation and heat-affected zone of polydimethylsiloxane films based on comprehensive surface analysis

Phenolic resin plate precision cutting by ultraviolet nanosecond laser ablation regulation

Experimental Investigation of Polymeric Material Removal by Low Diffraction Laser Beam

Composition conversion and parameters influence of nanosecond ultraviolet laser cutting polystyrene film

Laser ablation behavior and mechanism of polyimide by UV irradiation

Precision cutting of PDMS film with UV-nanosecond laser based on heat generation-diffusion regulation

Controlled photothermal ablative processing of commercial polymers minimizing undesired thermal effects under high frequency femtosecond laser irradiation

State-Of-The-Art and Trends in CO2 Laser Cutting of Polymeric Materials-A Review

Optimization of femtosecond laser cutting of a biodegradable polymer for medical devices manufacturing

The role of absorption mechanism on the optimization of processing commercial polymers under high repetition rate femtosecond laser irradiation

Effects of Femtosecond Laser Micromachining on the Surface and Substrate Properties of Poly-Lactic Acid (PLA)

The Impact of Selected Laser-Marking Parameters and Surface Conditions on White Polypropylene Moldings

Preparation of high-quality three-dimensional microstructures on polymethyl methacrylate surfaces by femtosecond laser micromachining and thermal-induced micro-leveling

EUV ablation of organic polymers at a high fluence