Cutting of polyethylene terephthalate (PET) film by 355 nm nanosecond laser

Congyi Wu,Min Li,Yu Huang,Youmin Rong
DOI: https://doi.org/10.1016/j.optlastec.2020.106565
2021-01-01
Abstract:<p>Special-shaped polyethylene terephthalate (PET) films are widely used in the electronics industry, and high-quality cuts is one of the core parameters for expanding scope of PET applications. In this article, 355 nm nanosecond laser is used to obtain a high-quality PET cuts. First, the laser cutting quality evaluation system based on the straightness, the width of the cuts, and the size of the heat affected zone (HAZ) was defined. Then, the influence of laser cutting parameters on the cut's quality was analyzed by 3 factors and 5 level orthogonal experiment, and high-quality cuts (width 25.2 ± 3.6 μm, HAZ 18.4 ± 2.2 μm, straightness 2.9 ± 0.32 μm) was obtained under the optimal process parameter combination. Finally, the interaction mechanism between nanosecond UV laser and PET film with heating carbonization and hot melt as the core was explored, and the effect of laser cutting process parameters on the quality of the cuts was analyzed based on this mechanism.</p>
optics,physics, applied
What problem does this paper attempt to address?
### Problems the Paper Aims to Solve This paper aims to address the demand for high-quality cutting of polyethylene terephthalate (PET) films in the electronics industry. Specifically, the paper explores the method of using a 355-nanometer nanosecond laser to cut PET films to achieve high precision, low heat-affected zone (HAZ), and good linearity in cutting results. With the increasing application demands in fields such as full-screen organic light-emitting diode (OLED) smartphones, higher requirements are being placed on the cutting quality of PET films, including cutting precision (≤30μm) and heat-affected error (≤50μm). Therefore, the goal of this study is to achieve high-quality PET film cutting by optimizing laser cutting parameters. ### Main Research Content 1. **Establishing a Cutting Quality Evaluation System**: - Defined a cutting quality evaluation system based on linearity, cutting width, and the size of the heat-affected zone (HAZ). 2. **Orthogonal Experimental Analysis**: - Designed an orthogonal experiment with 3 factors and 5 levels to analyze the effects of laser repetition rate (LRR), laser cutting speed (LCS), and laser cutting times (LCT) on cutting quality. - Determined the optimal combination of cutting parameters through orthogonal experiments, achieving the smallest cutting width (25.2 ± 3.6μm) and HAZ (18.4 ± 2.2μm). 3. **Interaction Mechanism Between Laser and PET Film**: - Explored the interaction mechanism between nanosecond UV laser and PET film, mainly involving heating carbonization and thermal melting processes. - Analyzed the specific impact of laser cutting parameters on cutting quality to further understand the interaction mechanism between laser and thermoplastic materials. ### Conclusion 1. **Interaction Mechanism**: - Nanosecond UV laser removes material through heating carbonization, and thermal diffusion causes the PET film around the cutting path to melt, forming a solidified heat-affected zone (HAZ). 2. **Orthogonal Experimental Results**: - As the laser repetition rate (LRR) and laser cutting times (LCT) increase and the laser cutting speed (LCS) decreases, the linearity of the cut gradually improves. The best linearity is 2.82μm, corresponding to the parameter combination of 5 (200kHz)-1 (10mm/s)-5 (50). - The trends in cutting width and HAZ width are similar. When the parameter combination is 5 (200kHz)-3 (50mm/s)-3 (30), the cutting width (25.2 ± 3.6μm) and HAZ (18.4 ± 2.2μm) reach their minimum values. ### Significance This study provides theoretical and technical support for high-quality PET film cutting, helping to expand the application range of PET films in the electronics industry, especially in flexible electronic devices that require high-precision cutting. By optimizing laser cutting parameters, cutting quality and production efficiency can be significantly improved.