The use of vacuum refining to separate Ca, Al, and P from crude metallurgical grade silicon
Xiaocong Deng,Lei Zhou,Kuixian Wei,Wenhui Ma
DOI: https://doi.org/10.1016/j.vacuum.2022.111581
IF: 4
2022-10-13
Vacuum
Abstract:Crude metallurgical grade silicon (C-MG-Si) is produced by electric furnace smelting and must be purified before being used to produce organosilicon monomers and polysilicon. In this paper, the separation of Ca, Al and P from C-MG-Si by vacuum refining was studied. First, the direct vacuum refining of C-MG-Si was carried out at 1723 K and 3 × 10 −3 - 5 × 10 −3 Pa. After refining for 2.5 hours, the removal efficiency of Ca, Al, and P reached 82.56%, 52.91%, and 79.17%, respectively. The combination of Ca, Al, and O was stable under the experimental conditions, and oxidized CaAl 2 Si 2 O 8 eventually reacted with Ca and transformed into CaSiO 3 , which was deposited in the products. The oxidation refining pretreatment of C-MG-Si was carried out before vacuum refining and removed 91.24% Ca and 77.08% Al, including elemental and oxidized Ca and Al. Then, the same vacuum refining procedure was carried out on the MG-Si produced by pretreatment, and the cumulative removal efficiency of Ca, Al, and P reached 98.08%, 83.85%, and 79.17%, respectively. This study shows that vacuum refining can replace or complement oxidation refining to purify C-MG-Si.
materials science, multidisciplinary,physics, applied