Abstract:In order to transform the crystalline form of Ca2SiO4 (C2S) in phosphorus-containing slag from monoclinic β-polycrystalline to square γ-polycrystalline, a volume expansion of about 11% was generated, which caused the phosphorus-containing slag to undergo self-powdering. The CaO-SiO2-Al2O3-MgO-MnO-P2O5-FeO slag system was analyzed using FactSage7.1 thermodynamic software, and the effects of different P2O5, FeO and basicity on the mineral phase composition of slag system were analyzed in the range of 1300~1700 °C. It was shown that P2O5, FeO and basicity all have an effect on the composition of the mineral phases. When the mass fraction of P2O5 in the slag was lower than 0.25%, it had less effect on the transformation of C2S crystalline structure. When the P2O5 content was higher than 0.25%, it was favorable to the generation of low-melting-point substances, but the P2O5 in the slag reacted with C2S in the silicate phase, making P5+ solidly soluble in C2S, inhibiting the transformation of β-C2S to γ-C2S and hindering the self-powdering of the slag. The FeO content in the slag system ranged from 20% to 28%, and as the FeO content increased, the C2S content in the silicate phase decreased from 33.3% to 25.9%, while the temperature at which the silicate was completely dissolved into the liquid phase decreased from 1600 °C to 1500 °C and the complete melting temperature of the slag decreased. The low FeO content facilitates the self-powdering of slag. In the high-phosphorus slag, at temperatures below 1450 °C, with the increase of basicity, the proportion of C2S in the silicate phase first increased and then decreased. With basicity at 1.8; the highest content of silicate phase, accounting for 33.7%; and the temperature exceeding 1450 °C, the silicate phase dissolved into the liquid phase, which is conducive to the removal of phosphorus from the slag, achieving the self-powdering of high-phosphorus slag.

A Novel Process for Separation of Magnetite and Phosphorous Phases from a CaO–SiO2–FeO–P2O5 Slag

Wet magnetic separation of phosphorus containing phase from modified BOF slag

A novel process for the direct utilization of copper slag and phosphate rock by compound modification and coreduction

Synchronous enrichment of phosphorus and iron from a high-phosphorus oolitic hematite ore to prepare Fe-P alloy by direct reduction-magnetic separation process

Thermodynamic Analysis of Mineral Phase Composition of Steel Slag System

New Slag for Nickel Matte Smelting Process and Subsequent Fe Extraction

Study on Separation of Iron from Waste Slag of Pyrite Processing

Separation and recovery of phosphorus from steelmaking slag via a selective leaching–chemical precipitation process

Recovery of iron from high phosphorus oolitic iron ore using coal-based reduction followed by magnetic separation

A Kinetic Study on Selective Leaching of Phosphorus from Dephosphorization Slag

Effect of Iron Phase Evolution on Copper Separation from Slag Via Coal-Based Reduction

An Innovative Technique for Comprehensive Utilization of High Aluminum Iron Ore via Pre-Reduced-Smelting Separation-Alkaline Leaching Process: Part I: Pre-Reduced-Smelting Separation to Recover Iron

The Function of Ca(Oh)(2) and Na2co3 As Additive on the Reduction of High-Phosphorus Oolitic Hematite-Coal Mixed Pellets

Phosphorus partitioning and recovery of low-phosphorus iron-rich compounds through physical separation of Linz-Donawitz slag

Slag design and optimization for iron capturing platinum group metals from alumina-based spent catalysts

KEY FACTORS FOR THE SEPARATION OF SILICON AND IRON DURING PHOSPHORUS RECOVERY FROM SLAG DISCHARGED FROM THE DOUBLE-SLAG REFINING PROCESS

Recovery of valuable elements from pyrite pyrolysis slag using magnetic separation-flotation technique

Efficient extraction of phosphate from dephosphorization slag by hydrochloric acid leaching

Separation of Iron and Calcium from a BSSF Steelmaking Slag Through Acid Leaching

Fusion Separation of Vanadium-Titanium Magnetite and Enrichment Test of Ti Element in Slag

Recovery of iron and calcium aluminate slag from high-ferrous bauxite by high-temperature reduction and smelting process