Abstract:In this study, a novel process was established for extraction of Fe and Al from a complex high aluminum iron ore (33.43% Fetotal and 19.09% Al2O3). The main steps in the proposed process included pre-reducing high alumina iron ore and subsequent smelting to produce pig iron and rich-alumina slag, followed by alkaline leaching of the slag to obtain sodium aluminate solution and a clean slag. When smelting the pre-reduced high alumina iron ore pellets at 1625 °C for 30 min with a slag basicity of 0.40, the pig iron yielded 97.08% Fe and extracted 0.13% Al2O3, together with an iron recovery of 94.54%. In addition, more than 68.93% Al2O3 was recovered by leaching the slag, which was achieved by firstly roasted the slag at 900 °C for 2 h and then alkaline leaching at 95 °C for 2 h with a liquid-to-solid ratio of 10 mL/g. In addition, the alkaline leaching slag could potentially be used as raw material for construction purpose, which mainly consisted of SiO2 and CaO.

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve This paper aims to address the efficient extraction of iron and aluminum from High Aluminum Iron Ore (HAIO). Specifically, the research team has developed an innovative technology that comprehensively recovers iron and aluminum from complex HAIO through a Pre-Reduced-Smelting Separation-Alkaline Leaching Process. ### Background and Challenges 1. **Increased Resource Demand**: With the rapid growth in demand for metals, the global reserves of high-quality ores are rapidly decreasing. 2. **Characteristics of High Aluminum Iron Ore**: HAIO is a complex multi-metal resource widely distributed in nature, especially in China, Australia, India, and Indonesia. This ore typically contains 5-20% Al₂O₃ and 30-60% Fe, making it difficult to use directly for ironmaking. 3. **Limitations of Traditional Methods**: - **Physical Beneficiation**: It is difficult to effectively remove aluminum due to the complex distribution and fine particle size of aluminum minerals. - **Bioleaching**: Although it has some effect on separating iron and aluminum, the results are poor, especially compared to the smelting process, and it takes too long. - **Smelting Process**: Existing smelting processes can effectively recover iron, but the recovery rate of aluminum is low, and the smelting slag is difficult to utilize effectively. ### Research Objectives 1. **Improve Iron Recovery Rate**: Increase the recovery rate and grade of iron through the pre-reduced-smelting separation process. 2. **Efficient Extraction of Aluminum**: Efficiently extract aluminum from smelting slag through the alkaline leaching process and produce clean slag that can be used in the cement industry. 3. **Economic and Environmental Feasibility**: Develop an economically viable and environmentally friendly comprehensive utilization technology for HAIO. ### Main Steps 1. **Pre-Reduction**: Pre-reduce HAIO pellets at a specific temperature to generate metallic iron and aluminum-containing slag. 2. **Smelting Separation**: Smelt and separate the pre-reduced pellets to further increase the iron recovery rate. 3. **Alkaline Leaching**: Treat the smelting slag with alkaline leaching to extract aluminum and produce clean slag. ### Experimental Results - **Iron Recovery Rate**: Smelting at 1625°C for 30 minutes resulted in pig iron containing 97.08% iron, with 0.13% Al₂O₃ extracted, achieving an iron recovery rate of 94.54%. - **Aluminum Recovery Rate**: By first calcining at 900°C for 2 hours and then alkaline leaching at 95°C for 2 hours with a liquid-solid ratio of 10 mL/g, an Al₂O₃ recovery rate of over 68.93% was achieved. - **Application of Clean Slag**: The slag after alkaline leaching mainly consists of SiO₂ and CaO, which can be used as raw materials for building materials. ### Conclusion This study proposes an innovative comprehensive utilization technology for HAIO. Through the Pre-Reduced-Smelting Separation-Alkaline Leaching Process, efficient recovery of iron and aluminum is achieved, with high economic and environmental feasibility.

An Innovative Technique for Comprehensive Utilization of High Aluminum Iron Ore via Pre-Reduced-Smelting Separation-Alkaline Leaching Process: Part I: Pre-Reduced-Smelting Separation to Recover Iron

Optimizing iron separation and recycling from iron tailings: A synergistic approach combining reduction roasting and alkaline leaching

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Leaching of aluminum and iron from boiler slag generated from a typical Chinese Steel Plant

Recovery of aluminum oxide and iron oxide from aluminum electrolysis iron-rich cover material and preparation of aluminum fluoride

Extraction of aluminum and iron from boiler slag by sulfuric acid

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Enrichment and Recovery Fe-containing Phases from High Iron Gibbsite Ore Based on Metallized Reduction and Magnetic Separation

Synchronous enrichment of phosphorus and iron from a high-phosphorus oolitic hematite ore to prepare Fe-P alloy by direct reduction-magnetic separation process

Recovery of iron and calcium aluminate slag from high-ferrous bauxite by high-temperature reduction and smelting process

Recovery of iron from high phosphorus oolitic iron ore using coal-based reduction followed by magnetic separation

Aluminum–iron separation in high‐acid leaching solution and high‐purity alumina preparation

A novel approach for extracting lithium from overhaul slag by low temperature roasting – water leaching

A Novel Method to Remove Iron Impurity from Aluminum

Innovative methodology for the utilization of low-grade pyrite cinder containing heavy metals via hydrothermal alkali melting followed by chlorination roasting

Innovative Methodology for Comprehensive Utilization of Iron Ore Tailings: Part 1. the Recovery of Iron from Iron Ore Tailings Using Magnetic Separation after Magnetizing Roasting.

Manganese and Aluminium Recovery from Ferromanganese Slag and Al White Dross by a High Temperature Smelting-Reduction Process

A new iron recovery and dephosphorization approach from unroasted high‐phosphorus oolitic hematite ore via a facile chemical beneficiation process

The Preparation of High-Purity Iron (99.987%) Employing a Process of Direct Reduction–Melting Separation–Slag Refining

Rare earth element recovery and aluminum-rich residue production from high alumina fly ash by alkali pre-desilication enhance the mechanochemical extraction process

A novel process for the direct utilization of copper slag and phosphate rock by compound modification and coreduction