Abstract:Steelmaking slag, a significant by-product of steelmaking, contains a certain amount of phosphorus, which makes it a potential phosphate source. To achieve its high value-added utilization, the P-concentrated C2S–C3P solid solution in slag is commonly separated. In this study, we adopted a selective leaching–chemical precipitation process to recover P from steelmaking slag. The effects of the acid, pH, and valence of Fe in slag on the leaching characteristics of P were first investigated. Chemical precipitation was then adopted to extract P from the leachate. The characteristics of the final product were evaluated. The results indicate that the P-concentrated solid solution was readily leached, whereas the Fe-rich magnesioferrite was resistant to dissolution in each acid solution. In view of the utilization of the residue and reducing the production costs, hydrochloric acid was considered the optimum leaching agent for dissolving the slag. The dissolution of steelmaking slag in the hydrochloric acid solution increased with a decrease in pH. In addition, 81.6% of the P in slag was dissolved at pH 3, whereas the Fe leaching was negligible, exhibiting an improved selective leaching. Further, the P-removed steelmaking slag can be reutilized in a steel plant to achieve waste-free steelmaking. In the following precipitation at pH 7, most of the P in the leachate was transformed into an insoluble calcium phosphate. This process provides more than a 70% P recovery from steelmaking slag. The P2O5 content in the product obtained reached 20.2 mass%, which can be applied as a fertilizer.

Separation of Iron and Calcium from a BSSF Steelmaking Slag Through Acid Leaching

Extraction of aluminum and iron from boiler slag by sulfuric acid

Leaching of aluminum and iron from boiler slag generated from a typical Chinese Steel Plant

Innovative Process for Strategic Metal Recovery from Electric Arc Furnace Slag by Alkaline Leaching

Separation of silicon and iron in copper slag by carbothermic reduction-alkaline leaching process

Separation and recovery of phosphorus from steelmaking slag via a selective leaching–chemical precipitation process

Efficient Separation and Recovery of Vanadium, Titanium, Iron, Magnesium, and Synthesizing Anhydrite from Steel Slag

Characterization of a Chromium-Bearing Carbon Steel Electric Arc Furnace Slag after Magnetic Separation to Determine the Potential for Iron and Chromium Recovery

Efficient extraction and separation of zinc and iron from electric arc furnace dust by roasting with FeSO<sub>4</sub>?7H<sub>2</sub>O followed by water leaching

Recovery of Iron and Aluminum from Bauxite Residue by Carbothermic Reduction and Slag Leaching

Extraction of Valuable Components from Ti-Bearing Blast Furnace Slag Using Sulfuric Acid Calcination Process

Extraction of Valuable Metals from Titanium-bearing Blast Furnace Slag by Acid Leaching

A Novel Process for Separation of Magnetite and Phosphorous Phases from a CaO–SiO2–FeO–P2O5 Slag

A Novel Process for Simultaneous Extraction of Iron, Vanadium, Manganese, Chromium, and Titanium from Vanadium Slag by Molten Salt Electrolysis

Recovery of iron from EAF smelter slags via hydrochloric acid leaching and solvent extraction using trioctyl phosphine oxide

Integration of Modified Solvay Process for Sodium Bicarbonate Synthesis from Saline Brines with Steelmaking for Utilization of Electric Arc Furnace Slag in CO2 Sequestration and Reagent Regeneration

Manganese and Aluminium Recovery from Ferromanganese Slag and Al White Dross by a High Temperature Smelting-Reduction Process

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis

An unconventional approach for the efficient recovery of iron, cobalt, copper and silicon from copper slag

Selective dissolution and kinetics of leaching zinc from lime treated electric arc furnace dust by alkaline media