Abstract:In the present work, the impact of ZrO2 gate dielectric thickness on the electrical performance of TiO2 thin film transistors (TFTs) is systematically investigated. Exhaustive electrical measurements on TFTs, metal–insulator–metal, and metal–oxide–semiconductor capacitors are carried out with varying ZrO2 dielectrics of different thicknesses. It is found that the ZrO2 possesses an outstanding thickness scalability, providing reliable dielectric properties under an ultrathin physical thickness of 5 nm, while further reduction in ZrO2 thickness would lead to a breakdown of the TFTs, indicating the physical limitations for the ultrathin ZrO2 dielectrics. The TiO2 TFTs with the 5 nm-thick ZrO2 dielectric exhibit an enhanced electrical performance, including a high on/off current ratio (I on/I off) of 7.7 × 108, a nearly ideal subthreshold (SS) of 72 mV/dec, and a high electron mobility (μeff) of 5.74 cm2·V–1·s–1 under an ultralow voltage of 2 V. Such prominent electrical characteristics with a battery-drivable low-voltage operation prove the suitability of the TiO2 TFTs for Internet of Things applications. This comprehensive study, revealing the behaviors of leakage current, oxide capacitance, oxide charges, and interface traps with respect to the ZrO2 thickness, sheds light on the quality and scalability of the ZrO2 dielectrics that can be extended to other channel materials, and also offers a framework for evaluating the material quality of other dielectrics. Furthermore, from a material point of view, the underlying physical reasons for the excellent ZrO2 thickness scalability are believed to be (1) the smooth surfaces of TiO2 and ZrO2, (2) the well-structured ZrO2 without detectable oxygen-related defects, and (3) the large conduction band offset between ZrO2 and TiO2. Overall, this study not only shows that the TiO2 TFTs hold great potential to empower future IoT applications, but also provides important guidance regarding dielectric scaling and quality evaluation in the nanometer scale.

Impact of ZrO 2 Dielectrics Thickness on Electrical Performance of TiO 2 Thin Film Transistors with Sub-2 V Operation

Fully solution-induced high performance indium oxide thin film transistors with ZrOx high-k gate dielectrics

Enhancement of electrical properties of solution-processed oxide thin film transistors using ZrO<sub>2</sub> gate dielectrics deposited by an oxygen-doped solution

Low-voltage, Solution-Processed InZnO Thin-Film Transistors with Enhanced Performance Achieved by Bilayer Gate Dielectrics

Low-Voltage High-Stability InZnO Thin-Film Transistor Using Ultra-Thin Solution-Processed ZrO Dielectric

Effects of various oxygen partial pressures on Ti-doped ZnO thin film transistors fabricated on flexible plastic substrate

Electrical Properties of Wide Bandgap ZnMgO and Fabrication of Transparent Thin Film Transistors

Advancements in Metal Oxide Thin Film Quality in Solution-Processed High-κ Dielectrics for High-Performance Transistors

The Influence of Channel Layer Thickness on the Electrical Properties of Zno Tfts

Surface Modification on Solution Processable ZrO2 High-k Dielectrics for Low Voltage Operations of Organic Thin Film Transistors

Effective Evaluation Strategy Toward Low Temperature Solution-Processed Oxide Dielectrics for TFT Device

Enhanced Performance of ZnO Thin-Film Transistors with ZnO Dual-Active-layer

Feasibility of Atomic Layer Deposited AlZrOx Film to Achieve High Performance and Good Stability of ZnSnO-TFT

Solution Processable High Quality ZrO2 Dielectric Films for Low Operation Voltage and Flexible Organic Thin Film Transistor Applications

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al2O3 Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

Fully solution-processed low-voltage aqueous In2O3 thin-film transistors using an ultrathin ZrO(x) dielectric.

Zirconium-Aluminum-Oxide Dielectric Layer with High Dielectric and Relatively Low Leakage Prepared by Spin-Coating and the Application in Thin-Film Transistor

TiSiOx Gate Dielectrics Produced by Reactive Sputtering for High Performance InGaZnO Thin Film Transistors

Solution-Processed Zirconium Oxide Gate Insulators for Top Gate and Low Operating Voltage Thin-Film Transistor

Approaching Subthreshold-Swing Limit for Thin-Film Transistors by Using a Giant-Dielectric-constant Gate Dielectric

Solution-Processed Indium-Zinc-Oxide Thin-Film Transistors Based On Anodized Aluminum Oxide Gate Insulator Modified With Zirconium Oxide