Abstract:G/G modules with POE were found to be more durable than those with EVA or transparent backsheet. The high resistivity POE inhibits sodium migration through the interfaces under negative and silver migration under positive bias, decreasing risk of PIDs and transmittance loss as compared to EVA. Interfacial adhesion strength reduced for both EVA and POE encapsulants resulting in similar risks of delamination under the damp heat conditions. Glass/glass (G/G) photovoltaic modules are quickly rising in popularity, but the durability of modern G/G packaging has not yet been established. In this work, we examine the interfacial degradation modes in G/G and glass/transparent backsheet modules under damp heat (DH) with and without system bias voltage, comparing emerging polyolefin elastomer (POE) and industry‐standard poly(ethylene‐co‐vinyl acetate) (EVA) encapsulants. We investigate the transport of ionic species at cell/encapsulant interfaces, demonstrating that POE limits both sodium and silver ion migration compared with EVA. Changes to the chemical structures of the encapsulants at the cell/encapsulant interfaces demonstrate that both POE and EVA are more susceptible to degradation in modules with a transparent backsheet than in the G/G configuration. Adhesion testing reveals that POE and EVA have comparable critical debond energies after the DH exposures regardless of system bias polarity. The results of this study indicate that the interfacial degradation mechanisms of G/G appear to be similar to those of conventional glass/backsheet modules. For emerging materials, our results demonstrate that POE offers advantages over EVA but that transparent backsheets may accelerate encapsulant degradation due to increased moisture ingress when compared with the G/G structure.

Lower LCOE achievement of silicon heterojunction solar modules with low water vapor transmission rate encapsulants

Chemical and mechanical interfacial degradation in bifacial glass/glass and glass/transparent backsheet photovoltaic modules

Light-induced performance of SHJ solar modules under 2000 h illumination

Encapsulation improvement and stability of ambient roll-to-roll slot-die-coated organic photovoltaic modules

From performance measurements to molecular level characterization: Exploring the differences between UV and DH weathering of PV modules

Efficient and reliable encapsulation for perovskite/silicon tandem solar modules

Enhancing photovoltaic modules encapsulation: Optimizing lamination processes for Polyolefin Elastomers (POE) through crosslinking behavior analysis

Encapsulation of PV Modules Using Ethylene Vinyl Acetate Copolymer as the Encapsulant

Potential-induced degradation of encapsulant-less p-type crystalline Si photovoltaic modules

Encapsulation-free crystalline silicon photovoltaic modules and their hygrothermal and thermal-cycle tolerance

Nondestructive Single‐Glass Vacuum Lamination Encapsulation for Perovskite Solar Cells with Long‐Term Stability

Properties and degradation behaviour of polyolefin encapsulants for photovoltaic modules

First principles modeling of polymer encapsulant degradation in Si photovoltaic modules

Early‐stage identification of encapsulants photobleaching and discoloration in crystalline silicon photovoltaic module laminates

Visible-light-driven Fe-catalyzed Alkylation for Synthesizing Functionalized Polyolefin Elastomers As Advanced Encapsulants in Photovoltaic Modules

UV‐induced degradation of high‐efficiency silicon PV modules with different cell architectures

Reduction of lead leakage from damaged lead halide perovskite solar modules using self-healing polymer-based encapsulation

Predicting the Lifetime of HJT Modules Towards the Outdoor Real-World Environment

Development of Amorphous/Microcrystalline Silicon Tandem Thin-Film Solar Modules with Low Output Voltage, High Energy Yield, Low Light-Induced Degradation, and High Damp-Heat Reliability

A research review on the encapsulants with high transmittance character

Thermo-mechanical stress modeling and experimental investigation on micro-cracks in tilling ribbon photovoltaic modules during lamination and mechanical load test