Abstract:Degradation of module encapsulant mechanical characteristics that lead to embrittlement and delamination remains a leading cause of failure in solar modules. Extending module lifetimes beyond 30 years requires advanced predictive modeling that includes the fundamental materials degradation pathways and their dependence on operating temperature, UV, and moisture. We present a time‐dependent multiscale mechanics model based on detailed molecular degradation reaction kinetics that connects the encapsulant bond density and interfacial bond density with its mechanical properties and adhesion energy. Photovoltaic (PV) modules are subjected to environmental stressors (UV exposure, temperature, and humidity) that cause degradation within the encapsulant and its interfaces with adjacent glass and cell substrates. To save experimental time and to enable long‐term assessment with intensive degradation only taking place after many years, the development of predictive models is indispensable. Previous works have modeled the delamination of the ethylene vinyl acetate (EVA) encapsulant/glass and encapsulant/cell interfaces under field aging conditions with fundamental photochemical degradation reactions that lead to molecular scission and loss of interfacial adhesion, characterized by the fracture resistance, Gc. However, these models were fundamentally limited in that the following aspects were not incorporated: (i) molecular crosslinking in the field, (ii) synergistic autocatalytic interactions of degradation mechanisms, (iii) connection between degraded encapsulant structure and its mechanical properties, and (iv) rigorous treatment of the plasticity contribution to Gc with finite element models. Here, we present a time‐dependent multiscale model that addresses these limitations and is applicable to a wide range of encapsulants and interfaces. For the reference EVA encapsulant and its interfaces with the glass and cell, the presented model predicts an initial rise in Gc in the first 3 years of field aging from crosslinking, then a subsequent sharp decline from degradation mechanisms. We used nanoindentation to measure the changes in EVA mechanical properties over exposure time to tune the model parameters. The model predictions of Gc and mechanical properties match with experimental data and show an improvement compared to previous models. The model can even predict switches in failure interfaces, such as the observed EVA/cell to EVA/glass transition. We also conducted a sensitivity analysis study by varying the degradation and crosslinking kinetic parameters to demonstrate their effects on Gc. Model extensions to polyolefin elastomer‐ and silicone‐encapsulants and their interfaces are also demonstrated.

Thermo-mechanical stress modeling and experimental investigation on micro-cracks in tilling ribbon photovoltaic modules during lamination and mechanical load test

Test on mechanical and electrical behavior of composite of flexible thin-film solar cells and PVDF membrane

Sequential thermomechanical stress and cracking analysis of photovoltaic modules with full and half-cut cells

Finite Element Modeling, Thermal–Mechanical Coupling Analysis, and Demonstration of Multibusbar Half-Cell Double-Glass Overlapping Photovoltaic Module During Lamination

Thermo-mechanical stress modelling and fracture analysis on ultra-thin silicon solar cell based on super multi-busbar PV modules

Thermo-mechanical behavior assessment of smart wire connected and busbarPV modules during production, transportation, and subsequent field loading stages

Evaluation of Surface Crack Formation in Photovoltaic Backsheets Using Fragmentation and Finite Element Simulations

Experimental study on micro-crack initiation in photovoltaic polycrystalline silicon wafer

Unveiling the Failure Mechanism of Electrical Interconnection in Thermal-Aged PV Modules

The application of fracture mechanics to failure analysis of photovoltaic solar modules

Inhibited Crack Development by Compressive Strain in Perovskite Solar Cells with Improved Mechanical Stability

Modelling and experimental investigations of microcracks in crystalline silicon photovoltaics: A review

Mechanical Analysis of the Quasi-Static and Dynamic Composite Action in PV Modules with Viscoelastic Encapsulant

Thermal Residual Stress Analysis of Soldering and Lamination Processes for Fabrication of Crystalline Silicon Photovoltaic Modules

Study of the Twelve Busbar Technology and the Stress-Induced Degradation Within the Solar Modules

Predicted Thermal Stresses in A Trimaterial Assembly with Application to Silicon-Based Photovoltaic Module

Interlaminar Mechanical Performance of a Multi-Layered Photovoltaic-Thermoelectric Hybrid Device

Predicting encapsulant delamination in photovoltaic modules bridging photochemical reaction kinetics and fracture mechanics

Encapsulation strategies for mechanical impact and damp heat reliability improvement of lightweight photovoltaic modules towards vehicle-integrated applications

A multi-physics and multi-scale numerical approach to microcracking and power-loss in photovoltaic modules

Simulation and Experimental Analysis of Temperature Profiles and Crosslinking in PV Module Lamination