Abstract:Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (Cf/C) composite for spark plasma sintering, two kinds of commercially pure α-Al2O3 powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (Tsg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al2O3 powder and 1400 °C for the 3 μm Al2O3 powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al2O3 compact can reach ∼80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth.

Effects of Al2O3 doping on the microstructural evolution and densification process of AZO targets

Study on the preparation and the film-forming properties of Mo-and Al-doped ZnO ceramic targets

Two-Step Sintering of Aluminum-Doped Zinc Oxide Sputtering Target by Using A Submicrometer Zinc Oxide Powder

Effects of MgO doping concentration on densification and microstructure of flash sintered α-Al2O3 ceramics

The Densification, Microstructure, and Electrical Properties of Aluminum-Doped Zinc Oxide Sputtering Target for Transparent Conductive Oxide Film

Effect of Sintering Temperature on Densification of GZO Ceramic Target Prepared by Pressureless Sintered

Microstructure and Electrical Properties of Al-doped ZnO Thin Films

Sintering Kinetics Involving Densification and Grain Growth of 3D Printed Ce–ZrO2/Al2O3

Preparation And Properties For Aluminum-Doped Zinc Oxide Powders With The Coprecipitation Method

In-Situ Doping Preparation of Al-Doped Zno Films Via Pulsed Laser Co-Ablation of Zn and Al Targets with Assistance of Oxygen Plasma

Preparation and Properties of Aluminum-Doped Zinc Oxide Ultrafine Powders

Study of sintering mechanism and characteristics of ZBO target

Effects of deposition power and pressure on the crystallinity of Al-doped ZnO thin films at glass substrates by low temperature RF magnetron sputtering

Effects of doping cations on the densification and microstructure of flash-sintered α-Al2O3

Preparing superdense ZAO target by doping Al2O3 nanopowder

Pressureless-sintering Behavior of Nanocrystalline ZrO2–Y2O3–Al2O3 System

Effect of ZrO2 and MgO doping on microstructure and properties of translucent alumina fabricated by rapid vacuum sintering

Effects of Al doping on the optical and electrical properties of pre-synthesized ZnO powders by solid state method

Effect of Y2O3 and ZnO co-doping on the densification and properties of magnesium aluminum spinel

Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering

Study on Aluminum Concentration on Optical and Electrical Properties of AZO Thin Films Fabricated by Ultrasonic Spray Pyrolysis