Abstract:The FeAl/Al 2 O 3 composites were fabricated by hot-pressing process in this research. The Fe-Al intermetallics compounds powders were fabricated by mechanical alloying and heat treatment. The FeAl powders and Al 2 O 3 powders were mixed and the FeAl/Al 2 O 3 composite powders were prepared. The FeAl/Al 2 O 3 composites bulks were fabricated by hot-pressing process at 1300°C for 2h under the pressure of 35MPa. The phase composition and microstructure of the FeAl intermetallics compounds powders produced by mechanical alloying and heat treatment were investigated. The phase composition and microstructure of the FeAl/Al 2 O 3 composites produced by hot-pressing process were investigated. The XRD patterns results showed that the Fe-Al intermetallics compounds powders were fabricated by mechanical alloying for 60h. The FeAl intermetallics compounds powders were fabricated by heat treatment at 800°C, 900°C and 1000°C. The microstructure showed that the mean particles size of the FeAl intermetallics compounds powders produced by mechanical alloying and heat treatment was rather fine and about 4-5μm. The XRD patterns results showed that there existed FeAl phase and Al 2 O 3 phase in sintered composites. The FeAl/Al 2 O 3 composites bulks exhibited the homogenous and compact microstructure. The mean particles size of FeAl was about 4-5μm and the mean particles size of Al 2 O 3 was about 4-5μm. The microstructure of the FeAl/Al 2 O 3 composites became more homogenous and compact with the increase of FeAl content.

Preparation of Fe Coating Al2O3 Nanometer Composite Powder and its Mechanical Properties after Hot Press Sintering

Preparation of Fe Coating Al<sub>2</sub>O<sub>3</sub> Nanometer Composite Powder and its Mechanical Properties after Hot Press Sintering

Effect of Sintering Temperature on Microstructure and Mechanical Properties of Hot-Pressed Fe/FeAl2O4 Composite

Preparation and Sintering of Nano Fe Coated Si 3 N 4 Composite Powders

Preparation and mechanical properties of Fe3Al/Al2O3 nano-/micro-composite

Effect of Fe on the Microstructure and Mechanical Properties of Fe/FeAl2O4 Cermet Prepared by Hot Press Sintering

Preparation and Mechanical Properties of FeMo-Al2O3 Composite Ceramics

Preparation Nanostructured FeAl2O4-Al2O3-Fe Composite Coating by SHS Plasma Spraying Technology

Study of Hot-press Sintering Process of Nanometer Cu-Al_2O_3 Composite

Preparation & characterization of composite with micron AI coating in nanometer Fe particles

Preparation of NiAl2O4/Al2O3 composite nanopowder

Preparation and reparation and mechanical properties of nanocobalt coated AL2O3-TIC composites

Nano-Al2O3 reinforced Fe-Cr-Ni composites fabricated by reactive hot pressing

Preparation and microstructure of nano-size cobalt-coated Al2O3/TiC composites

Investigation of Phase Composition and Microstructure of the FeAl/Al<sub>2</sub>O<sub>3</sub> Composites Fabricated by Mechanical Alloying and Hot-Pressing Process

Effect of heat treatment on the microstructure and property of cold-sprayed nanostructured FeAl/Al2O3 intermetallic composite coating

Preparation of Fe-coated Si3N4 Composite Powder by Heterogeneous Precipitation-Thermal Reduction Process

Study on Preparation and Mechanical Properties of Fe3Al–20 Wt.%al2o3 Composites

Preparation and Interface Investigation of Fe/Al2o3p Composite Activated by Ni and Ti

Preparation of FeAl/TiC Composites by Reactive Hot Pressing