Abstract:The surface mechanical attrition treatment was taken to fabricate the gradient structure in AZ31 magnesium alloy sheet. Microstructural investigations demonstrate the formation of dual gradients with respect to grain size and orientation, where the microstructural sizes decreased from several microns to about 200 nm from center area to treated surface, while the c-axis gradually inclined from being vertical to treated plane towards parallel with it. According to tensile results, the gradient structured sample has yield strength of 305 MPa in average, which is increased by about 4 times when compared with its coarse-grained counterpart. Meanwhile, contrary to quickly failure after necking in most traditional magnesium alloys, the failure process of gradient structure appears more gently, which makes it has 6.5% uniform elongation but 11.5% total elongation. The further comparative tensile tests for separated gradient layers and corresponding cores demonstrate that the gradient structured sample has higher elongation either in uniform or in post-uniform stages. In order to elucidate the relationship between mechanical properties and deformation mechanisms for this dual gradient structure, the repeated stress relaxation tests and pole figure examinations via X-ray diffraction were conducted in constituent gradient layer and corresponding core, as well as gradient structured sample. The results show that the pyramidal dislocations in dual gradient structure are activated through the whole thickness of sample. Together with the contribution of grain-size gradient, more dislocations are activated in dual gradient structure under tensile loading, which results in stronger strain hardening and hence higher tensile ductility.

Enhancing tensile properties of extruded AZ31 rod by introducing gradient bimodal microstructure

Preparation and Characterization of Mg Alloy Rods with Gradient Microstructure by Torsion Deformation

Evolution of Gradient Microstructure in an Extruded AZ31 Rod During Torsion and Annealing and Its Effects on Mechanical Properties

Improving Tensile and Compressive Properties of an Extruded AZ91 Rod by the Combined Use of Torsion Deformation and Aging Treatment

Gradient structure induced simultaneous enhancement of strength and ductility in AZ31 Mg alloy with twin-twin interactions

Grain Refinement Mechanisms in Gradient Nanostructured AZ31B Mg Alloy Prepared Via Rotary Swaging

Microstructure, Texture and Mechanical Properties of Extruded AZ31 Mg Alloy During Small Strain Multi-Directional Forging with Gradient Cooling

Influence of Torsion Route on the Microstructure and Mechanical Properties of Extruded AZ31 Rods

Refining the Microstructure, Modifying the Texture and Enhancing the Toughness of AZ31B Alloy Rod by the Extrusion and Upsetting

Improving tensile and compressive properties of magnesium alloy rods via a simple pre-torsion deformation

Enhancing tensile strength of Cu by introducing gradient microstructures via a simple torsion deformation

Enhanced Mechanical Properties of a Hot-Extruded AZ80 Mg Alloy Rod by Pre-Treatments and Post-Hot Compression

Formation of Gradient Microstructure and Elimination of Tension-Compression Yield Asymmetry of the Extruded Mg-4.58Zn-2.6Gd-0.18Zr Alloy Via Free-End Torsion

Mechanical Properties and Deformation Mechanism of Mg-Al-Zn Alloy with Gradient Microstructure in Grain Size and Orientation

Influence of direct extrusion and torsional deformation on microstructure and properties of magnesium alloys

Microstructure, Texture and Mechanical Properties of AZ31 Magnesium Alloy Fabricated by High Strain Rate Biaxial Forging

Strengthening and toughening of extruded magnesium alloy rods by combining pre-torsion deformation with subsequent annealing

Effect of Bimodal Microstructure on the Tensile Properties and Fracture Toughness of Extruded Mg-9Gd-4Y-0.5Zr Alloy

Gradient microstructure and superior strength–ductility synergy of AZ61 magnesium alloy bars processed by radial forging with different deformation temperatures

Ductility enhancement mechanism of AZ31 magnesium alloy with through-thickness symmetrical gradient structure prepared by hard plate rolling

Microstructure and Mechanical Properties of AZ31 Mg Alloy Produced by a New Compound Extrusion Technique