Effect of stress ratio and overload on mixed-mode crack propagation behaviour of EA4T steel

Shuancheng Wang,Bing Yang,Shuwei Zhou,Yuanzhi Wang,Shoune Xiao

DOI: https://doi.org/10.1016/j.engfracmech.2024.110210

IF: 5.4

2024-06-03

Engineering Fracture Mechanics

Abstract:The influence of stress ratio ( R- ratio) and overload effect on the mixed mode fatigue crack growth (FCG) behaviour is experimentally assessed in this study. Mixed-mode FCG tests were conducted on EA4T steel, involving variations in R -ratios, overload types, and overload interval (OLI) cycle times. The results showed that the crack propagation prediction model, incorporating plasticity and roughness-induced crack closure effects as proposed in previous work based on the model of Christopher and Pokluda et al., outperforms four traditional models when fitting experimental data under different R- ratio conditions. Considering the impact of the R- ratio, the original mixed model was modified which shows an improvement of approximately 7 % in fitting experimental data. The ranking of overload retardation effects within overload types was as follows: single overload (SOL) > double overload (DOL) > multiple overload (MOL). The interval cycles incorporated within the overload sequence can weaken the crack closure effect caused by the crack tip overload. A smaller OLI can lead to the retardation effect of the preceding overload being overshadowed by the influence of the subsequent overload, thus diminishing the retardation effect. Increasing the OLI reduces interference among the retardation effects of different overloads, resulting in smaller interference zones for each overload retardation effect. The crack tip opening displacement was proposed as the delay parameter, and the rationality of the delay parameter was verified by combining it with the test data. The parameter effectively reflects the retardation state and aligns well with the test results

mechanics