Abstract:Defects introduced during additive manufacturing currently control fatigue resistance and lead to a large scatter in lifetime, with pancake shaped lack of fusion (LOF) defects being particularly potent. In this study the fatigue crack propagation life of selective laser-melted (SLM) AlSi10Mg alloy is considered in cases where single cracks and multiple cracks can initiate from LOF defects under high cycle fatigue (HCF). Firstly, the aspect ratios of initially long fatigue cracks were determined for critical LOF defects obtained from X-ray CT renderings using the critical defect regularization method, and the response surface method used to obtain the stress intensity factor of the crack front quickly and continuously. Then a single crack propagation model considering the evolution of the crack aspect ratio established to predict the crack propagation life which is in good agreement within in situ X-ray CT imaging of the crack front when a single crack is dominant. The crack propagation phase was predicted to represent 35–60% of the total fatigue life representing a larger fraction at high stress amplitudes. Multiple cracks were found to initiate cracks at the larger stress amplitudes. In cases where multiple cracks arise this is non-conservative and so a synergistic multiple fatigue crack growth (smFCG) model was developed based on multiple defects measured a priori by X-ray CT to depict the competitive cracking effect. Compared with the single crack model, the smFCG model predicts a shorter propagation life (by 5–10%) when multiple defects are involved since it considers all the initial defects within the crack initiation region. Given the propensity of large numbers of defects in AM material this approach may be more appropriate in many cases.

Short fatigue crack growth: overload-induced acceleration/retardation behavior

DIC-based Studies of the Overloading Effects on the Fatigue Crack Propagation Behavior of Ti-6Al-4V ELI Alloy

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Study on the multi‐scale online fatigue crack deformation and growth behaviors under overload in Q&P steel

Effect of stress ratio and overload on mixed-mode crack propagation behaviour of EA4T steel

Fatigue crack growth under mixed mode I-II loading with a single tensile overload at negative load ratios

Retardation mechanisms and modeling of fatigue crack growth of a high-strength steel after single overload

Near-tip Strain Evolution and Crack Closure of Growing Fatigue Crack under a Single Tensile Overload

Verification of stress transfer mechanism in fatigue crack growth under overload

STUDY OF FATIGUE CRACK GROWTH RETARDATION, CRACK TIP DEFORMATION AND CRACK CLOSURE UNDER SINGLE OVERLOAD APPLICATION FOR A537 STEEL

Experimental investigation of overload effects on fatigue crack growth behaviour of 7050‐T7451 aluminium alloy

Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Overload-induced anisotropy of fatigue crack growth in laser deposited Ti-6Al-4V alloy

A unified prediction model for physically small crack and long crack growth based on modified CTOD

In-situ investigation of fatigue crack growth behavior of 34CrNi3Mo high-strength steel

In situ X-ray imaging of fatigue crack growth from multiple defects in additively manufactured AlSi10Mg alloy

In situ SEM-DIC technique and its application to characterize the high-temperature fatigue crack closure effect

On the Study of Fatigue Crack Propagation in the Time Domain