Abstract:Defects introduced during additive manufacturing currently control fatigue resistance and lead to a large scatter in lifetime, with pancake shaped lack of fusion (LOF) defects being particularly potent. In this study the fatigue crack propagation life of selective laser-melted (SLM) AlSi10Mg alloy is considered in cases where single cracks and multiple cracks can initiate from LOF defects under high cycle fatigue (HCF). Firstly, the aspect ratios of initially long fatigue cracks were determined for critical LOF defects obtained from X-ray CT renderings using the critical defect regularization method, and the response surface method used to obtain the stress intensity factor of the crack front quickly and continuously. Then a single crack propagation model considering the evolution of the crack aspect ratio established to predict the crack propagation life which is in good agreement within in situ X-ray CT imaging of the crack front when a single crack is dominant. The crack propagation phase was predicted to represent 35–60% of the total fatigue life representing a larger fraction at high stress amplitudes. Multiple cracks were found to initiate cracks at the larger stress amplitudes. In cases where multiple cracks arise this is non-conservative and so a synergistic multiple fatigue crack growth (smFCG) model was developed based on multiple defects measured a priori by X-ray CT to depict the competitive cracking effect. Compared with the single crack model, the smFCG model predicts a shorter propagation life (by 5–10%) when multiple defects are involved since it considers all the initial defects within the crack initiation region. Given the propensity of large numbers of defects in AM material this approach may be more appropriate in many cases.

Near-tip Strain Evolution and Crack Closure of Growing Fatigue Crack under a Single Tensile Overload

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

STUDY OF FATIGUE CRACK GROWTH RETARDATION, CRACK TIP DEFORMATION AND CRACK CLOSURE UNDER SINGLE OVERLOAD APPLICATION FOR A537 STEEL

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

A Study on Fatigue Crack Closure Associated with the Growth of Long Crack in a New Titanium Alloy

Effect of loading conditions on short fatigue crack propagation behaviours in cast Al Si alloys

Fatigue Crack Growth Rates and Crack Tip Opening Loads in CT Specimens Made of SDSS and Manufactured Using WAAM

Experimental study of crack tip deformation under fatigue load

Measurement and simulation of strain fields around crack tips under mixed-mode fatigue loading

Study on the crack nucleation mechanism of Ti-2Al-2.5Zr alloy in low cycle fatigue: Quasi in-situ experiments and crystal plasticity simulation

Short fatigue crack growth: overload-induced acceleration/retardation behavior

In situ X-ray imaging of fatigue crack growth from multiple defects in additively manufactured AlSi10Mg alloy

An Investigation of Small-crack and Long-crack Propagation Behavior in Titanium Alloy TC4 and Aluminum Alloy 7475-T7351

In-situ investigation of fatigue crack growth behavior of 34CrNi3Mo high-strength steel

Effect of surface high-density twinned structure on the fatigue crack initiation of Ti-6Al-4V

Three-dimensional Quantitative in Situ Study of Crack Initiation and Propagation in AA 6061 Aluminum Alloy Sheets Via Synchrotron Laminography and Finite-Element Simulations

Fatigue crack growth under mixed mode I-II loading with a single tensile overload at negative load ratios

Strain Field Around Individual Dislocations Controls Failure