Abstract:In the serviced components of a 7075 aluminum alloy, the propagation of fatigue crack can be retarded because of the overload effect; however, the corresponding retardation mechanisms are complex. To provide further insights into the retardation mechanisms of 7075 aluminum alloys, this study addresses the crack tip damage response of a cracked 7075 aluminum alloy under an overload effect. Based on the dual-scale modeling approach and the damage-coupled crystal plasticity model, the effect of the microstructure of a 7075 aluminum alloy on the damage behavior ahead of the crack tip under an overload was studied. The factors affecting fatigue damage accumulation ahead of the crack tip, such as dislocation density, the variation in the activities of slip systems, and the orientation effect of the nearest neighbor grains, are described. The results show that for the 7075 aluminum alloy, the compressive residual stress induced by the overload effect not only decreases the number of activated slip systems, but also lowers the rate of increase in dislocation density. This causes a decrease in fatigue damage accumulation during deformation. Moreover, the overload effect decreases the slip system activity as well as the resultant plastic slip; however, the decrease in plastic slip varies with the grain orientation, indicating that the overload effect depends on the grain orientation. It can also be found that both the damage strain energy release rate and lattice strain are influenced by the orientation of the nearest neighbor grains, which can eventually affect the overload effect. These findings contribute to understanding the retardation mechanisms from a microscopic perspective and provide guidance on improving the material design of a 7075 aluminum alloy to some extent.

Crack growth behavior of U71MnG rail steel under overload conditions described using a dislocation correction model

Study on Fatigue Crack Growth in Rail Steel at Numerical and Experimental Approaches

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

DIC-based Studies of the Overloading Effects on the Fatigue Crack Propagation Behavior of Ti-6Al-4V ELI Alloy

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Effect of stress ratio and overload on mixed-mode crack propagation behaviour of EA4T steel

Retardation mechanisms and modeling of fatigue crack growth of a high-strength steel after single overload

STUDY OF FATIGUE CRACK GROWTH RETARDATION, CRACK TIP DEFORMATION AND CRACK CLOSURE UNDER SINGLE OVERLOAD APPLICATION FOR A537 STEEL

Mixed mode crack growth behaviour considering plasticity-induced and roughness-induced closure

Study on the multi‐scale online fatigue crack deformation and growth behaviors under overload in Q&P steel

Experimental and numerical insights into fatigue crack propagation of railway component with gradient residual stress

Short fatigue crack growth: overload-induced acceleration/retardation behavior

Study on fatigue damage tolerance of rail steel materials using peridynamics

Dynamic mechanical behaviors of pearlitic U71MnG rail steel: Deformation mechanisms and constitutive model

Crystal plasticity modeling of grain boundary softening and fatigue in U75V pearlite steel under low strain conditions: A study of cyclic rolling contact fatigue

Influence of initial crack on fatigue crack propagation with mixed mode in U71Mn rail subsurface

Verification of stress transfer mechanism in fatigue crack growth under overload

The Overload Effect on the Crack Tip Damage Mechanism in a 7075 Aluminum Alloy

A cyclic visco-plastic constitutive model for the ratcheting behavior of U75VG rail steel under a wide range of loading rates

Uniaxial and non-proportionally multiaxial ratcheting of U71Mn rail steel: experiments and simulations

Experimental study on fatigue crack growth of QSTE420TM steel with a single dwell-overload and a combined prediction model