Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

A miniaturized thin‐plate low cycle fatigue test method at elevated temperature

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Cyclic Stress-Strain Response During Isothermal and Thermomechanical Fatigue

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Low cycle fatigue and creep-fatigue behavior of a high temperature alloy on smooth and notched specimens

Low cycle fatigue and creep-fatigue interaction behavior of 2.25CrMoV steel at high temperature

Fatigue behavior of molybdenum alloy under hightemperature thermomechanical stress cycles

Effect of Temperature on High‐cycle Fatigue and Very High Cycle Fatigue Behaviours of a Low‐strength Cr–Ni–Mo–V Steel Welded Joint

Low Cycle Fatigue Crack Growth Behavior of Modified Rotor Steel under High-Temperature

On Creep Fatigue Interaction of Components at Elevated Temperature

Low Cycle Fatigue of 9-12% Cr Steel at Elevated Temperature: Cyclic Deformation Behavior and Life Assessment

A comparative study of low cycle fatigue behavior and microstructure of Cr-based steel at room and high temperatures

Effects of temperature and strain amplitude on low-cycle fatigue behavior of 12Cr13 martensitic stainless steel

Unravelling the Effects of Ratcheting and Constraint on the Cyclic Behaviour of a Martensitic Steel under Elevated Temperature

Low Cycle Fatigue, Creep and Creep-Fatigue Interaction Behavior of a TiAl Alloy at High Temperatures