Abstract:The main purpose of this study is to determine, via a three dimensions Finite Element analysis (FE), the stress and strain fields at the inner surface of a tubular specimen submitted to thermo-mechanical fatigue. To investigate the surface finish effect on fatigue behaviour at this inner surface, mechanical tests were carried out on real size tubular specimens under various thermal loadings. X ray measurements, Transmission Electron Microscopy observations and micro-hardness tests performed at and under the inner surface of the specimen before testing, revealed residual internal stresses and a large dislocation microstructure gradient in correlation with hardening gradients due to machining. A memory effect, bound to the pre-hardening gradient, was introduced into an elasto-visco-plastic model in order to determine the stress and strain fields at the inner surface. The temperature evolution on the inner surface of the tubular specimen was first computed via a thermo-elastic model and then used for our thermo-mechanical simulations. Identification of the thermo-mechanical model parameters was based on the experimental stabilized cyclic tension-compression tests performed at 20^{\circ}C and 300^{\circ}C. A good agreement was obtained between numerical stabilized traction-compression cycle curves (with and without pre-straining) and experimental ones. This 3 dimensional simulation gave access to the evolution of the axial and tangential internal stresses and local strains during the tests. Numerical results showed: a decreasing of the tangential stress and stabilization after 40 cycles, whereas the axial stress showed weaker decreasing with the number of cycles. The results also pointed out a ratcheting and a slightly non proportional loading at the inner surface. The computed mean stress and strain values of the stabilized cycle being far from the initial ones, they could be used to get the safety margins of standard design related to fatigue, as well as to get accurate loading conditions needed for the use of more advanced fatigue analysis and criteria.

Cyclic Stress-Strain Response During Isothermal and Thermomechanical Fatigue

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Thermal-Mechanical Fatigue Lifetime Prediction of an Austenitic Stainless-Steel

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Depth-Sensing Indentation-Based Studies of Surface Mechanical Behavior and Fatigue Damage Evolution of an Austenitic Stainless Steel Subjected to Cyclic Straining

Cyclic deformation mechanism and fracture behaviour of 316L stainless steel under thermomechanical fatigue loading

Stress–Strain Response of AISI H13 Steel Subjected to Cyclic Thermomechanical Loading

Thermo-mechanical FE model with memory effect for 304L austenitic stainless steel presenting microstructure gradient

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Experimental Investigation and Numerical Modelling of the Cyclic Plasticity and Fatigue Behavior of Additively Manufactured 316L Stainless Steel

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Isothermal and thermomechanical fatigue behavior of 316LN stainless Steel: Effects of strain amplitude

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

High Temperature Isothermal and Thermomechanical Fatigue on A Molybdenum-Based Alloy

Fatigue behavior of molybdenum alloy under hightemperature thermomechanical stress cycles

Lifetime prediction of time-dependent thermomechanical fatigue of high temperature alloys