Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Experimental investigations on combined high and low cycle fatigue: Material-level specimen design and strain response characteristics

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Low-cycle fatigue test of CFT and CCFT columns

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Experimental and Numerical Study of Combined High and Low Cycle Fatigue Performance of Low Alloy Steel and Engineering Application

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Combined high and low cycle fatigue analysis of FGH96 alloy under high temperature conditions

Strain‐Controlled Low‐Cycle Fatigue Behavior of a Superalloy Considering Extensive Temperature Range and Stress Concentration

Investigation of low cycle fatigue crack propagation behavior of 316H steel at 550°C based on cyclic response and damage accumulation: experiment and modelling

Damage Proportion Analysis of the Combined High and Low Cycle Fatigue Based on the Continuum Damage Mechanics

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses