The Effect of Drying and Thickness of TiO2 Electrodes on the Photovoltaic Performance of Dye-Sensitized Solar Cells

Arman Sedghi,Hoda Nourmohammadi Miankushki

DOI: https://doi.org/10.1016/s1452-3981(23)06545-8

IF: 1.541

2015-04-01

International Journal of Electrochemical Science

Abstract:Dye-sensitized solar cells (DSSC) are based on the absorption of photons by dye, and the transfer of these to TiO2 electrodes. The microstructure and defects of TiO2 electrodes are vital for the fabrication of high efficiency dye-sensitized solar cells. These properties strongly relate to the TiO2 electrode method of fabrication and its parameters. In this research, the effect of drying and thickness of the nanocrystallineTiO2 electrodes were investigated. Nanocrystalline TiO2 thin films of different thicknesses were deposited on FTO-coated glass substrates using a tape casting method. Then, these electrodes were dried at different temperatures (130°C and 70°C) at different heating rate. Subsequently, the electrodes were immersed into a dye solution. After dyeing, the cells were assembled using the dye-covered TiO2 electrodes and platinum-coated FTO and iodine electrolytes. These samples were characterized by SEM, TGA, FTIR, OM and the cell performance then measured by a solar light simulator at an intensity of 1000 W.m-2. Drying the electrodes at different temperature and different heating rate showed that the solar cells with a TiO2 electrode dried at 130°C, and at lower heating rate gave a higher short-circuit current density and open circuit voltage, with a higher overall conversion efficiency of 5.1%. The effect of the thickness of TiO2 films on the parameters of DSSCs was also investigated. Results showed that by increasing the thickness of the TiO2 films, absorption of the N719 dye through the TiO2 layers increased to a more optimum level, so that power conversion efficiency (η) of 7.51 % was obtained.

electrochemistry