Abstract:Hydrothermally synthesized TiO2 nanotubes (TNTs) with a diameter of approximately 10 nm and a length of 250 nm are successfully employed in dye-sensitized solar cells (DSSCs) based on N719 dye and iodide/triiodide electrolyte and exhibiting an efficiency of 7.6% at 1 sun illumination. Randomly oriented TiO2 nanotubes are deposited on FTO glass by the electrophoretic deposition method, and the thickness of the TNT layer and hence the solar cell performance have been shown to depend on the deposition time and the nanotube concentration in the electrolyte solution. The highest efficiency is obtained for the solar cell fabricated with the 6-minute electrophoretically deposited TiO2 film having a film thickness of 6 μm. These pristine TNT photoelectrodes exhibit a short-circuit current density (Jsc), an open-circuit voltage (Voc), a fill factor (FF) and an efficiency (η) of 2.4 mA cm−2, 899 mV, 78% and 1.7%, respectively. TiCl4 treatment of pristine TNT photoelectrodes enhances the Jsc, Voc, FF and η to 13.2 mA cm−2, 819 mV, 70.4% and 7.6%, respectively. The TiCl4 treatment is found to be vital for the enhancement of the solar cell performance of hydrothermally synthesised TiO2 nanotube based devices. Enhancement of electron lifetime is noted after treatment of bare TiO2 nanotubes with 0.5 M TiCl4 solution. The electron transport resistance, electron lifetime and charge recombination properties of bare and TiCl4 treated TiO2 nanotubes are investigated by electrochemical impedance measurements. The increased performance of the DSSC fabricated with TiCl4 treated TNTs is due to several factors favouring the enhancement of efficiency. These include the dye loading amount, the decrease in electron transport resistance, the increase in density of states and enhancement of light scattering.

Effect of TiO2 electrode thickness on photovoltaic properties of dye sensitized solar cell based on randomly oriented Titania nanotubes

Hierarchical Submicroflowers Assembled from Ultrathin Anatase TiO2 Nanosheets As Light Scattering Centers in TiO2 Photoanodes for Dye-Sensitized Solar Cells

EFFECTS OF TiO2 FILM THICKNESS AND ELECTROLYTE CONCENTRATION ON PHOTOVOLTAIC PERFORMANCE OF DYE-SENSITIZED SOLAR CELL

Open-circuit voltage improvement by using TiO2 nanotubes as a working electrode of dye-sensitized solar cell

Influence of TiO2 Film Thickness on the Electrochemical Behaviour of Dye-Sensitized Solar Cells

Thickness-dependent electron transport performance of mesoporous TiO2 thin film for dye-sensitized solar cells

The Effect of Drying and Thickness of TiO2 Electrodes on the Photovoltaic Performance of Dye-Sensitized Solar Cells

Hydrothermally synthesized titania nanotubes as a promising electron transport medium in dye sensitized solar cells exhibiting a record efficiency of 7.6% for 1-D based devices

The effects of the thickness of TiO2 films on the performance of dye-sensitized solar cells

Effect of the Geometry of the Anodized Titania Nanotube Array on the Performance of Dye-Sensitized Solar Cells.

Effect of compressed TiO2 nanoparticle thin film thickness on the performance of dye-sensitized solar cells

The Effect of Optical Properties on Photovoltaic Performance in Dye-Sensitized Tio2 Nanocrystalline Solar Cells

Liquid phase deposition/anodizing of TiO2 nanotube working electrode for dye-sensitized solar cells

Influence Of Applied Voltage On Anodized Tio2 Nanotube Arrays And Their Performance On Dye Sensitized Solar Cells

Thickness effect of nanocrystal TiO2 photoanodes on Dye Sensitized Solar Cells (DSSC) performances

Photocurrent response loss of dye sensitized solar cells owing to top surface nanograss growth and bundling of anodic TiO2 nanotubes

Nitrogen-doped TiO2 Nanoparticles Better TiO2 Nanotube Array Photo-Anodes for Dye Sensitized Solar Cells

A Bilayer Structure of A Titania Nanoparticle/Highly-Ordered Nanotube Array for Low-Temperature Dye-Sensitized Solar Cells

Enhanced Efficiency for Dye-Sensitized Solar Cells Using A Surface-Treated Photo-Anode

TiO 2 nanoparticle seeds transformed into nanotubes for effective dye-sensitized solar cell application

Preparation and photoelectric performanceof high-aspect-ratio TiO 2 nanotube arrays film electrode