Abstract:Hydrothermally synthesized TiO2 nanotubes (TNTs) with a diameter of approximately 10 nm and a length of 250 nm are successfully employed in dye-sensitized solar cells (DSSCs) based on N719 dye and iodide/triiodide electrolyte and exhibiting an efficiency of 7.6% at 1 sun illumination. Randomly oriented TiO2 nanotubes are deposited on FTO glass by the electrophoretic deposition method, and the thickness of the TNT layer and hence the solar cell performance have been shown to depend on the deposition time and the nanotube concentration in the electrolyte solution. The highest efficiency is obtained for the solar cell fabricated with the 6-minute electrophoretically deposited TiO2 film having a film thickness of 6 μm. These pristine TNT photoelectrodes exhibit a short-circuit current density (Jsc), an open-circuit voltage (Voc), a fill factor (FF) and an efficiency (η) of 2.4 mA cm−2, 899 mV, 78% and 1.7%, respectively. TiCl4 treatment of pristine TNT photoelectrodes enhances the Jsc, Voc, FF and η to 13.2 mA cm−2, 819 mV, 70.4% and 7.6%, respectively. The TiCl4 treatment is found to be vital for the enhancement of the solar cell performance of hydrothermally synthesised TiO2 nanotube based devices. Enhancement of electron lifetime is noted after treatment of bare TiO2 nanotubes with 0.5 M TiCl4 solution. The electron transport resistance, electron lifetime and charge recombination properties of bare and TiCl4 treated TiO2 nanotubes are investigated by electrochemical impedance measurements. The increased performance of the DSSC fabricated with TiCl4 treated TNTs is due to several factors favouring the enhancement of efficiency. These include the dye loading amount, the decrease in electron transport resistance, the increase in density of states and enhancement of light scattering.

Open-circuit voltage improvement by using TiO2 nanotubes as a working electrode of dye-sensitized solar cell

Functions of Self-Assembled Ultrafine TiO2 Nanocrystals for High Efficient Dye-Sensitized Solar Cells

Construction of Efficient Photoanodes for Dye Sensitized Solar Cells: TiO2 Films with a Gradient Content of Graphene

Improved Performance of Dye Sensitized Solar Cells Using Cu-doped TiO2 As Photoanode Materials: Band Edge Movement Study by Spectroelectrochemistry

TiO 2 nanoparticle seeds transformed into nanotubes for effective dye-sensitized solar cell application

Effect of TiO2 electrode thickness on photovoltaic properties of dye sensitized solar cell based on randomly oriented Titania nanotubes

Hydrothermally synthesized titania nanotubes as a promising electron transport medium in dye sensitized solar cells exhibiting a record efficiency of 7.6% for 1-D based devices

Enhanced open-circuit voltage of dye-sensitized solar cells using Bi-doped TiO2 nanofibers as working electrode and scattering layer

Highly-Ordered Tio2 Nanotube Arrays with Double-Walled and Bamboo-Type Structures in Dye-Sensitized Solar Cells

Hybrid TiO2–SnO2 Nanotube Arrays for Dye-Sensitized Solar Cells

Growth of TiO2 Nanoflowers Photoanode for Dye-Sensitized Solar Cells

Enhanced Performance of Dye-Sensitized Solar Cells based on TiO2 Nanotube Membranes using Optimized Annealing Profile

The Preparation of TiO2 Nanotube by ZnO Nanorod Template Method and Application in Dye-Sensitized Solar Cells

Design and Preparation of Nano-Electrodes for Dye-Sensitized Solar Cell

Utilization of Titanate Nanotubes as an Electrode Material in Dye-Sensitized Solar Cells

High-efficiency dye-sensitized solar cells based on robust and both-end-open TiO2 nanotube membranes

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

TiO2 nanotube based dye-sensitized photoanode

Application of TiO2 nanoparticles coated multi-wall carbon nanotube to dye-sensitized solar cells

Nd-doped TiO2 Nanorods: Preparation and Application in Dye-Sensitized Solar Cells.

Electron Transport in Dye-Sensitized Solar Cells Based on TiO 2 Nanowires