Abstract:Dye-sensitized solar cells (DSSC) are based on the absorption of photons by dye, and the transfer of these to TiO2 electrodes. The microstructure and defects of TiO2 electrodes are vital for the fabrication of high efficiency dye-sensitized solar cells. These properties strongly relate to the TiO2 electrode method of fabrication and its parameters. In this research, the effect of drying and thickness of the nanocrystallineTiO2 electrodes were investigated. Nanocrystalline TiO2 thin films of different thicknesses were deposited on FTO-coated glass substrates using a tape casting method. Then, these electrodes were dried at different temperatures (130°C and 70°C) at different heating rate. Subsequently, the electrodes were immersed into a dye solution. After dyeing, the cells were assembled using the dye-covered TiO2 electrodes and platinum-coated FTO and iodine electrolytes. These samples were characterized by SEM, TGA, FTIR, OM and the cell performance then measured by a solar light simulator at an intensity of 1000 W.m-2. Drying the electrodes at different temperature and different heating rate showed that the solar cells with a TiO2 electrode dried at 130°C, and at lower heating rate gave a higher short-circuit current density and open circuit voltage, with a higher overall conversion efficiency of 5.1%. The effect of the thickness of TiO2 films on the parameters of DSSCs was also investigated. Results showed that by increasing the thickness of the TiO2 films, absorption of the N719 dye through the TiO2 layers increased to a more optimum level, so that power conversion efficiency (η) of 7.51 % was obtained.

The effect of hydro-thermal synthesis temperature on the dye sensitized TiO2 electrode

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Nanocrystalline titanium dioxide prepared by hydrothermal method and its application in dye-sensitised solar cells

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Effect of annealing temperature on nano-crystalline TiO2 for solar cell applications

Study on Sol-hydrothermal Synthesis of TiO_2 Nanoparticles and Their Photoelectric Properties Sensitized by Dye

Study on Sol-hydrothermal Synthesis of TiO<SUB>2</SUB> Nanoparticles and their Photoelectric Properties Sensitized by Dye: Study on Sol-hydrothermal Synthesis of TiO<SUB>2</SUB> Nanoparticles and their Photoelectric Properties Sensitized by Dye

EFFECT OF TEMPERATURE ON TiO_2 NANOPOWDERS PREPARED BY A HYDROTHERMAL METHOD

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Hydrothermal Synthesis of TiO2 Nanostructure Films and Their Photoelectrochemical Properties

Preparation of Transparent TiO2 Nanocrystalline Film for UV Sensor

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

The Effect of Drying and Thickness of TiO2 Electrodes on the Photovoltaic Performance of Dye-Sensitized Solar Cells

Effect of Annealing Temperature on the Photoelectrochemical Properties of Dye-Sensitized Solar Cells Made with Mesoporous TiO2 Nanoparticles

Optimization of Photoelectrode Introduced to Dye-Sensitized Solar Cells by Anodic Oxidative Hydrolysis

Effect of Annealing Temperature on TiO 2 Nanorod Films Prepared by dc Reactive Magnetron Sputtering for Dye-Sensitized Solar Cells

Influence of growth temperature on structural, optical, morphological and photoelectrochemical characteristics of vertically aligned hydrothermally synthesized TiO 2 nanorods.

Synthesis and Characterization of TiO_2 Nano-crystalline with Different Morphologies by Low-temperature Hydrothermal Method