Abstract:Strain controlled low cycle fatigue tests have been conducted in air to ascertain the influence of strain rate(ε = 4 × 10-6'to 4 × 10-3 s-1) and temperature(T = 750/850/950 °C) on LCF behavior of Alloy 617. A strain range of 0.6 pct and a symmetrical triangular wave form were employed for all the tests. Crack initiation and propagation modes were studied. Microstructural changes that occurred during fatigue deformation were evaluated and compared with the results obtained on isothermal aging. Deformation and damage mechanisms which influence the endurance have been identified. A reduction in fatigue life was observed with decreasing ε at 850 °C and with increasing temperature at ε = 4 × 10-5 s-1. Cyclic stress response varied as a complex function of temperature and strain rate. Fatigue deformation was found to induce cellular precipitation of carbides at 750 and 850 ‡. Dynamic strain aging characterized by serrated flow was observed at 750 °C (ε = 4 × 10-5 s-1) and in the tests at higher ε at 850 °C. Strengthening of the matrix due to dynamic strain aging of matrix dislocations by precipitation of M23C6 carbides led to fracture of grain boundary carbide films formed at 750 °C, producing brittle intergranular crack propagation. At 850 °C transgranular crack propagation was observed at the higher strain rates ε≥4× 10-4 s-1. At 850 and 950 °C even at strain rates of 4 × 10-5 s-1 or lower, life was not governed by intergranular creep rupture damage mechanisms under the symmetrical, continuous cycling conditions employed. Reduction of endurance at lower strain rates is caused by increased inelastic strain and intergranular crack initiation due to oxidation of surface connected grain boundaries.

A Mathematical Model for Competing Failure Modes in Strain Cycle Fatigue

Fatigue Life and Mechanistic Modeling of Interior Micro-Defect Induced Cracking in High Cycle and Very High Cycle Regimes

A Modified Normal Strain Ratio Fatigue Life Model Based on the Hybrid Approach of Critical Plane and Crystallographic Slip Theory

A New, Direct Approach Toward Modeling Thermo-Coupled Fatigue Failure Behavior of Metals and Alloys

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses

A Direct Approach Toward Simulating Cyclic and Non-Cyclic Fatigue Failure of Metals

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling

A New Life Prediction Model Based on Ductility Exhaustion Theory for High Temperature Low Cycle Fatigue of Turbine Disk Alloys

Probabilistic Modeling of LCF Failure Times Using an Epidemiological Crack Percolation Model

An engineering model of fatigue crack growth under variable amplitude loading

Evaluation of Size Effect in Low Cycle Fatigue for Q&T Rotor Steel

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Microstructure evolution, failure mechanism and life prediction of additively manufactured Inconel 625 superalloy with comparable low cycle fatigue performance

A New, Direct Approach Toward Modeling Rate-Dependent Fatigue Failure of Metals

Probabilistic fatigue modelling of metallic materials under notch and size effect using the weakest link theory

Numerical simulation of low cycle fatigue behavior, combining the phase‐field method and the Armstrong‐Frederick model

New ultra-low cycle fatigue model for metal alloys

Probabilistic modeling and simulation of multiple surface crack propagation and coalescence

A Continuous Low Cycle Fatigue Damage Model and Its Application in Engineering Materials

Damage Evolution Model Considering Fatigue Failure Factor Under Multiaxial Non-Proportional Loading

Experimental Study and Numerical Simulation on High Temperature & Low Cycle Short Fatigue Cracks under Multiaxial Stress States