Abstract:Competing fatigue failure between the surface and internal nucleation has been widely observed in metals under the high cycle fatigue regime. To characterize different boundary conditions in surface and internal grain aggregates, a hybrid statistical volume element model was developed by binding two identical periodic stochastic polycrystal microstructure cubes together and superimposing them with a new 2.5 directional periodic boundary condition afterwards. Additional isotropic elastic media was attached on the surface of the hybrid statistical volume element model to represent the oxide layer formed at elevated temperature. Microstructure-sensitive modeling with a crystal plasticity model was implemented by computing multiple hybrid statistical volume elements under two stress levels. The results implied that grains in the surface volume of the hybrid statistical volume element generally tended to deform more easily than their counterparts in the internal one, and the oxide layer had a weak effect in suppressing the surface deformation. It was also demonstrated that the combination of the 2.5 directional periodic boundary condition, additional oxide layer and nonlinear constitutive model jointly brought stochastic effect into the two identical microstructural cubes. Significant competition between the surface and internal nucleation was captured under both stress levels. Since the detrimental influence of oxidation in accelerating crack formation was not considered, the lifetimes from both types of nucleation were overlaid on each other. Given the disruption of the oxide layer under high stress levels, the simulation reproduced the experimental discovery that the probability of surface nucleation increases with the ascending stress level. It is also clarified that the oxide layer cannot prevent surface nucleation under low stress levels, rejecting the hypothesis of the impact of the oxide layer on complete internal nucleation.

Probabilistic modeling and simulation of multiple surface crack propagation and coalescence

An X-FEM Approach for Simulation of 3-D Multiple Fatigue Cracks and Application to Double Surface Crack Problems

Probabilistic Modeling of LCF Failure Times Using an Epidemiological Crack Percolation Model

Progress in Complex 2d and 3d Cohesive Fracture Modelling Considering Random Heterogeneity

A Failure-Dependence Related Stochastic Crack Growth Modeling Approach of Competing Cracking Mode

Numerical Simulation of the Multiple 3D Crack Propagation from the Countersunk Fastener Holes

Monte Carlo simulation of complex cohesive fracture in random heterogeneous quasi-brittle materials

Insights on low cycle fatigue crack formation and propagation mechanism: A microstructurally-sensitive modeling

Monte Carlo Simulation of Complex 2D Cohesive Fracture in Random Heterogeneous Quasi-Brittle Materials

A novel LCF lifetime model for PM superalloys considering crack energy differences induced by surface underconstraint

Microstructure-sensitive Modeling of Competing Failure Mode Between Surface and Internal Nucleation in High Cycle Fatigue

Numerical Simulation Of Multiple Cracking In Ansi 304 Stainless Steel Under Thermal Fatigue

Numerical Analyses Of Interaction Behavior Of Multiple Surface Cracks Using A Modified Creep-Damage Model And Fracture Mechanics Approach

A Probabilistic Model for Low-Cycle Fatigue Crack Initiation under Variable Load Cycles

Modeling of Fatigue Crack Propagation

A Multiscale Crack Iteration and Remeshing Model for Low-Cycle Crack Propagation Evaluation

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling

Probabilistic Modeling of Fatigue Crack Growth and Experimental Verification

Numerical simulation of fatigue crack propagation interacting with micro-defects using multiscale XFEM

Random Model of Fatigue Multi-Crack Propagation