Abstract:In this work, Cu-1.4 wt%Ta-Zr alloys with different Zr content (0, 0.1, 0.2 and 0.5 wt%) were fabricated by mechanical alloying combined with spark plasm sintering. The effect of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloy were characterized. Cu-Ta alloys composes of ultrafine equiaxed grains along with the uniformly dispersion of semi-coherent Ta nanoclusters and incoherent Ta coarse particles. As Zr is introduced into Cu-Ta alloy, the Ta precipitates were effectively refined, especially for the reduction of Ta coarse particles. The significant refinement effect of the grains is realized when Zr content reaches 0.2 wt%, and high-proportioned nano-sized grains are facilitated to form, along with the activation of a lot of twins and the formation of intermetallic composed of Cu and Zr. The dislocation density and strength increase remarkably with the increase of Zr content, and the highest strength (499 MPa for yield strength and 600 MPa for ultimate tensile strength) is achieved as the Zr content is up to 0.2 wt%. Compared with Cu-Ta alloy (382 MPa for yield strength and 560 MPa for ultimate tensile strength), the significant increment of 31% for the yield strength is successfully realized by Cu-Ta-0.2 wt%Zr alloy. Cu-Ta-0.2 wt%Zr alloys exhibit the excellent thermal stability, and the hardness keeps stable even the sample was annealed at 700 °C for 300 h, showing superior microstructural stability in comparison with Cu-Ta alloy (~4.5% reduction of the hardness after 300 h at 700 °C). The softening temperature of Cu-Ta-0.2 wt%Zr alloy is up to 1028 °C (1022 °C for Cu-Ta alloy) along with higher hardness than that of Cu-Ta alloy at the same annealing temperature. This study provides a new way to fabricate dispersion strengthened Cu alloys with high strength, exceptional thermal stability and softening resistance, which have great potential application value in the field of future fusion reactor.

Formation of superconductive supersaturated TaZr solid solutions by pulsed electron beam treatment

Preparation and Characterization of High-Entropy Alloy (TaNb)$_{1-x}$(ZrHfTi)$_x$ Superconducting Films

Preparation and Superconducting Properties of Thin Films of Some Binary Transition Metal Alloy Systems

Nonequilibrium Crystalline Phases Formed in the Co-Ta System by Ion-Beam Mixing

Pulsed excimer (KrF) laser induced crystallization of PbZr0.44Ti0.56O3 amorphous films

Formation of an Face-Centered Cubic Ta-Rich Solid Solution by Ion Beam Mixing in the Immiscible Ag-Ta System

Effects of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloys

Superconductivity in thermally annealed Ta-Nb-Hf-Zr-Ti high-entropy alloys

Phase Formation and Thermal Stability of Reactively Sputtered YTaO4-ZrO2 Coatings

Thermal stability of structure, microstructure and enhanced properties of Zr–Ta–O films with a low and high Ta content

Microstructure and elevated temperature properties of a refractory TaNbHfZrTi alloy

In situ $He^{+}$ irradiation of the double solid solution $(Ti_{0.5},Zr_{0.5})_{2}(Al_{0.5},Sn_{0.5})C$ MAX phase: Defect evolution in the 350-800 °C temperature range

Highly Thermal-Stable Amorphous TaSi2Cx Thin Films

Influence of Nb, Ta and Zr on the Interdiffusion Coefficients and Solid Solution Strengthening of γ-TiAl Single Phase Alloys

Phase transformations in Ti-Nb-Ta and Ti-Nb-Ta-Zr alloys

Structural phase transition in the Fe–Ta system studied by ion beam mixing

The Effect of Solution Heat Treatment Time on the Phase Formation and Selected Mechanical Properties of Ti-25Ta-xZr Alloys for Application as Biomaterials

Microstructure and properties of an equiatomic TaTiZr alloy

Formation of Non-Equilibrium Phases and Associated Structural Transition in the Pd-Ta System Induced by Ion Beam Mixing

Pulsed laser deposition of tantalum oxide thin films

Molecular beam epitaxy growth of superconducting tantalum germanide