Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Size controlled synthesis of gold nanoparticles using photochemically prepared seed particles

Seeded Growth Synthesis of Uniform Gold Nanoparticles with Controlled Diameters up to 220 nm

Synthesis and optical properties of size-controlled gold nanoparticles

Shape-controlled Synthesis of Highly Monodisperse and Small Size Gold Nanoparticles

Seed-Mediated Synthesis of Gold Tetrahedra in High Purity and with Tunable, Well-Controlled Sizes

Size‐Controlled Synthesis of Highly Monodisperse Gold Nanoparticles Without a Size‐Selection and Long Range Ordered 2‐D Arrangement

Size-Controlled Synthesis of Sub-10-nanometer Citrate-Stabilized Gold Nanoparticles and Related Optical Properties.

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

Size-Control of Monodispersing Gold Nanoparticles Via Stepwise Seed-Mediated Growth

Size controlled synthesis of 2-6 nm gold nanoparticles via controlling concentration of the reducing agent and temperature

Seed-mediated Synthesis of Gold Octahedra in High Purity and with Well-Controlled Sizes and Optical Properties.

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

Successive, Seed‐Mediated Growth for the Synthesis of Single‐Crystal Gold Nanospheres with Uniform Diameters Controlled in the Range of 5–150 Nm

Size-Controlled Synthesis Of Near-Monodisperse Gold Nanoparticles In The 1-4 Nm Range Using Polymeric Stabilizers

Prepartion of Gold Sols of Large Size Particles

Synthesis of Uniform and Stable Silver Nanoparticles by A Gold Seed-Mediated Growth Approach in A Buffer System

Seeded-growth synthesis of 20–60 nm monodisperse citrate-capped gold nanoparticles in a millifluidic reactor

In-Situ Seed-Mediated Growth of Polymer-Grafted Gold Nanoparticles.

Revitalizing the Frens Method to Synthesize Uniform, Quasi-Spherical Gold Nanoparticles with Deliberately Regulated Sizes from 2 to 330 Nm

Atomically Precise Nanoclusters Predominantly Seed Gold Nanoparticle Syntheses.

One-Pot, High-Yield Synthesis of Size-Controlled Gold Particles with Narrow Size Distribution