Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Prepartion of Gold Sols of Large Size Particles

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

Formation mechanism of nonspherical gold nanoparticles during seeding growth: roles of anion adsorption and reduction rate.

Size-controlled growth of colloidal gold nanoplates and their high-purity acquisition.

Seed-Mediated Growth of Large, Monodisperse Core-Shell Gold-Silver Nanoparticles with Ag-Like Optical Properties

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

Improved Size Control of Large Palladium Nanoparticles by A Seeding Growth Method

Seed-mediated Growth of Gold Nanoparticles Using Self-Assembled Monolayer of Polystyrene Microspheres As Nanotemplate Arrays

A Simple Method to Self-Assemble Two-dimensional and Three-dimensional Superlattices of Gold Nanoparticles

Atomically Precise Nanoclusters Predominantly Seed Gold Nanoparticle Syntheses.

One-step Seed-Mediated Growth of 30–150 Nm Quasispherical Gold Nanoparticles with 2-Mercaptosuccinic Acid As a New Reducing Agent

Controllable Synthesis of Gold Nanoparticles with Ultrasmall Size and High Monodispersity Via Continuous Supplement of Precursor.

A study on the sizes and concentrations of gold nanoparticles by spectra of absorption, resonance Rayleigh scattering and resonance non-linear scattering

Gold Nanorods Sol Prepared by Electrolysis

Reorganization of Gold Nanoprticles in Self-Assembled Nanostructures

Preparation of gold nanoparticles in a complete polymeric microfluidic reactor under UV irradiation

A Facile Route to Synthesize Gold Prisms Up to Micrometer Scale Based on Slow Reduction Methods

Seeded growth of monodisperse and spherical silver nanoparticles

Ammonium Bicarbonate Reduction Route to Uniform Gold Nanoparticles and Their Applications in Catalysis and Surface-Enhanced Raman Scattering

One-Pot, High-Yield Synthesis of Size-Controlled Gold Particles with Narrow Size Distribution