Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Formation mechanism of nonspherical gold nanoparticles during seeding growth: roles of anion adsorption and reduction rate.

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth

A Mechanistic Study on the Nucleation and Growth of Au on Pd Seeds with a Cubic or Octahedral Shape

Atomically Precise Nanoclusters Predominantly Seed Gold Nanoparticle Syntheses.

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

One-step Seed-Mediated Growth of 30–150 Nm Quasispherical Gold Nanoparticles with 2-Mercaptosuccinic Acid As a New Reducing Agent

Controlling the Formation of Au Nanoparticles Using Functionalized Molecular Buffer Layers

Formation and Stability of Gold Nanoflowers by the Seeding Approach: the Effect of Intraparticle Ripening

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

One-Pot Synthesis of Ultrasmooth, Precisely Shaped Gold Nanospheres via Surface Self-Polishing Etching and Regrowth

A Mechanism for the Self-Organization of Colloidal Gold Nanoparticles

Growth Mechanism of Flowerlike Gold Nanostructures: Surface Plasmon Resonance (SPR) and Resonance Rayleigh Scattering (RRS) Approaches to Growth Monitoring

In-situ self-assembly growth of controllable gold nanoparticles film

Reorganization of Gold Nanoprticles in Self-Assembled Nanostructures

Ammonium Bicarbonate Reduction Route to Uniform Gold Nanoparticles and Their Applications in Catalysis and Surface-Enhanced Raman Scattering

Seed-mediated Growth of Gold Nanoparticles Using Self-Assembled Monolayer of Polystyrene Microspheres As Nanotemplate Arrays

Characterization of Gold Nanoparticles Synthesized Using Sucrose by Seeding Formation in the Solid Phase and Seeding Growth in Aqueous Solution

Synthesis and growth mechanism of gold nanoplates with novel shapes

Insights into Initial Kinetic Nucleation of Gold Nanocrystals.

Quasi-spherical Silver Nanoparticles: Aqueous Synthesis and Size Control by the Seed-Mediated Lee–Meisel Method

Halide Anions As Shape-Directing Agents for Obtaining High-Quality Anisotropic Gold Nanostructures