Abstract:Growth kinetics and temporal size/shape evolution of gold nanocrystals by citrate reduction in boiling water were studied systematically and quantitatively. Results reveal that the size variation and overall reaction mechanism were mostly determined by the solution pH that was in turn controlled by the concentration of sodium citrate (Na3Ct) in the traditional Frens's synthesis. This conclusion was further confirmed by the reactions with variable pH but fixed concentrations of the two reactants, HAuCl4 and Na3Ct. Two substantially different reaction pathways were identified, with the switching point at pH = 6.2-6.5. The first pathway is for the low pH range and consists of three overlapping steps: nucleation, random attachment to polycrystalline nanowires, and smoothing of the nanowires via intra-particle ripening to dots. The second pathway that occurred above the pH switching point is consistent with the commonly known nucleation-growth route. Using the second pathway, we demonstrated a new synthetic route for the synthesis of nearly monodisperse gold nanocrystals in the size range from 20 to 40 nm by simply varying the solution pH with fixed concentrations of HAuCl4 and Na3Ct. The switching of the reaction pathways is likely due to the integration nature of water as a reaction medium. In the citrate reduction, the solution pH was varied by changing the initial HAuCl4/Na3Ct ratio. Consequently, when pH was higher than about 6.2, the very reactive [AuCl3(OH)]- would be converted to less reactive [AuCl2(OH)2]- and [AuCl(OH)3]-.

Size-Controlled Synthesis of Sub-10-nanometer Citrate-Stabilized Gold Nanoparticles and Related Optical Properties.

Synthesis of Highly Monodisperse Citrate-Stabilized Silver Nanoparticles of up to 200 nm: Kinetic Control and Catalytic Properties

Revitalizing the Frens Method to Synthesize Uniform, Quasi-Spherical Gold Nanoparticles with Deliberately Regulated Sizes from 2 to 330 Nm

Synthesis and optical properties of size-controlled gold nanoparticles

Size controlled synthesis of gold nanoparticles using photochemically prepared seed particles

Size Control of Gold Nanocrystals in Citrate Reduction: The Third Role of Citrate

New Insight Into the Size Tuning of Monodispersed Colloidal Gold Obtained by Citrate Method

Size focusing: a methodology for synthesizing atomically precise gold nanoclusters

Quasi-spherical Silver Nanoparticles: Aqueous Synthesis and Size Control by the Seed-Mediated Lee–Meisel Method

Size Control Synthesis of Monodisperse, Quasi-Spherical Silver Nanoparticles To Realize Surface-Enhanced Raman Scattering Uniformity and Reproducibility

Synthesis Of Monodisperse Quasi-Spherical Gold Nanoparticles In Water Via Silver(I)-Assisted Citrate Reduction

Morphological and size tuning of biogenic Ag and Au nanoparticles induced by laser irradiation

Size controlled synthesis of 2-6 nm gold nanoparticles via controlling concentration of the reducing agent and temperature

Size-Controlled Synthesis, Characterization, And Stability Of Dendrimer-Stabilized Silver Nanoparticles

Shape-controlled Synthesis of Highly Monodisperse and Small Size Gold Nanoparticles

Valence, Size, and Shape Control of Gold Nanoparticles Synthesized by Electron-Assisted Reduction

Syntheses and Characterization of Nearly Monodispersed, Size-Tunable Silver Nanoparticles over a Wide Size Range of 7-200 Nm by Tannic Acid Reduction.

Tuning the Size of Gold Nanoparticles in the Citrate Reduction by Chloride Ions

On the Interplay of Gold Nanoparticles and Small Molecules

Size‐Controlled Synthesis of Highly Monodisperse Gold Nanoparticles Without a Size‐Selection and Long Range Ordered 2‐D Arrangement

Rapid Seeded Growth of Monodisperse, Quasi-Spherical, Citrate-Stabilized Gold Nanoparticles Via H2o2 Reduction