Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Seeded Growth Synthesis of Uniform Gold Nanoparticles with Controlled Diameters up to 220 nm

Seed-mediated synthesis of silver nanocrystals with controlled sizes and shapes in droplet microreactors separated by air.

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

A Mechanistic Study on the Nucleation and Growth of Au on Pd Seeds with a Cubic or Octahedral Shape

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

Seeded-growth synthesis of 20–60 nm monodisperse citrate-capped gold nanoparticles in a millifluidic reactor

Atomically Precise Nanoclusters Predominantly Seed Gold Nanoparticle Syntheses.

One-step Seed-Mediated Growth of 30–150 Nm Quasispherical Gold Nanoparticles with 2-Mercaptosuccinic Acid As a New Reducing Agent

Formation mechanism of nonspherical gold nanoparticles during seeding growth: roles of anion adsorption and reduction rate.

Size-controlled growth of colloidal gold nanoplates and their high-purity acquisition.

One-step seeded growth of Au nanoparticles with widely tunable sizes.

Controllable Synthesis of Gold Nanoparticles with Ultrasmall Size and High Monodispersity Via Continuous Supplement of Precursor.

Seed-Mediated Growth of Large, Monodisperse Core-Shell Gold-Silver Nanoparticles with Ag-Like Optical Properties

Seed-mediated Growth of Gold Nanoparticles Using Self-Assembled Monolayer of Polystyrene Microspheres As Nanotemplate Arrays

One-Pot Synthesis of Ultrasmooth, Precisely Shaped Gold Nanospheres via Surface Self-Polishing Etching and Regrowth

Synthesis and optical properties of size-controlled gold nanoparticles

Formation and Stability of Gold Nanoflowers by the Seeding Approach: the Effect of Intraparticle Ripening

Seeded growth of monodisperse and spherical silver nanoparticles

Characterization of Gold Nanoparticles Synthesized Using Sucrose by Seeding Formation in the Solid Phase and Seeding Growth in Aqueous Solution

Improved Size Control of Large Palladium Nanoparticles by A Seeding Growth Method