Abstract:Au nanoparticles (NPs) of various sizes were synthesized by controlling the NP growth process. When the ratio of the HAuCl4 and NaBH4 solution concentrations was controlled, the experimental results showed that the average Au NP size decreased as the HAuCl4 concentration of the seed solution increased, owing to the increase in the number of Au seeds. The activity of the seed solution decreased as the additive volume of the HAuCl4 solution increased, resulting in the formation of large Au seeds. At low seed solution additive volumes, the peak absorbance wavelength and average size of the Au NPs decreased rapidly as the seed solution additive volume increased. The final size of the Au NPs with negatively charged Au seeds was relatively large since the size of the negatively charged Au seeds was relatively large. In addition, it was easier for the negatively charged seed solution to absorb Au atoms in the positively charged growth solution. A high ascorbic acid concentration was beneficial for improving the production of Au NPs. The average size of the Au seeds added to the growth solution increased gradually with the number of NPs grown, which resulted in an increase in the average Au NP size.

Size-Control of Monodispersing Gold Nanoparticles Via Stepwise Seed-Mediated Growth

A Mechanistic Study on the Nucleation and Growth of Au on Pd Seeds with a Cubic or Octahedral Shape

Shape-controlled Synthesis of Highly Monodisperse and Small Size Gold Nanoparticles

Improved Size Control of Large Palladium Nanoparticles by A Seeding Growth Method

Revitalizing the Frens Method to Synthesize Uniform, Quasi-Spherical Gold Nanoparticles with Deliberately Regulated Sizes from 2 to 330 Nm

Seeded Growth Synthesis of Uniform Gold Nanoparticles with Controlled Diameters up to 220 nm

Synthesis and optical properties of size-controlled gold nanoparticles

Size controlled synthesis of gold nanoparticles using photochemically prepared seed particles

Size‐Controlled Synthesis of Highly Monodisperse Gold Nanoparticles Without a Size‐Selection and Long Range Ordered 2‐D Arrangement

Successive, Seed‐Mediated Growth for the Synthesis of Single‐Crystal Gold Nanospheres with Uniform Diameters Controlled in the Range of 5–150 Nm

Rapid Seeded Growth of Monodisperse, Quasi-Spherical, Citrate-Stabilized Gold Nanoparticles Via H2o2 Reduction

Controlling the size and morphology of Au@Pd core-shell nanocrystals by manipulating the kinetics of seeded growth.

Synthesis of size-controlled monodisperse Pd nanoparticles via a non-aqueous seed-mediated growth

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth

Seed-Mediated Synthesis of Gold Tetrahedra in High Purity and with Tunable, Well-Controlled Sizes

Controllable Synthesis of Gold Nanoparticles with Ultrasmall Size and High Monodispersity Via Continuous Supplement of Precursor.

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

One-step Seed-Mediated Growth of 30–150 Nm Quasispherical Gold Nanoparticles with 2-Mercaptosuccinic Acid As a New Reducing Agent

High–Yield Production of Uniform Gold Nanoparticles with Sizes from 31 to 577 Nm Via One‐Pot Seeded Growth and Size‐Dependent SERS Property

Seed-mediated Synthesis of Gold Octahedra in High Purity and with Well-Controlled Sizes and Optical Properties.

Controlling The Growth Of Au On Icosahedral Seeds Of Pd By Manipulating The Reduction Kinetics