Solidification Process, Mechanical and Electrochemical Properties of Amorphous and Nanocrystalline Iron Alloy for a Power System Application

Xiaozhong Xu,Jiangang Li,Jiajie Yu,Xiaoqin Jiang,Gan Shao,

DOI: https://doi.org/10.20964/2021.08.39

IF: 1.541

2021-08-01

International Journal of Electrochemical Science

Abstract:Nanocrystalline alloy is widely used in power systems because of its advantages of high magnetic conductivity, low loss, high strength and high resistivity. The amorphous method was used to prepare iron with the best amorphous thin strip processing parameters: the size of circular quartz tube was 0.8 mm; the distance between the nozzle and the surface of copper roller was 0.5 mm; the linear speed of copper roller surface was 41 m/s; the pressure difference between the inside and outside of quartz tube was 0.03 MPa; the spray angle was 0°. The solidification of the Fe based nanocrystalline alloy was studied by the solidification morphology, X-ray diffraction analysis, magnetic properties and mechanical properties. According to EIS studies, a 360K undercooling temperature leads to an increase in the penetration of electrolyte ions into electrode structures due to the formation of a high surface area and a high electron-transfer rate. The experimental results show that the undercooling of the alloy melt can be significantly improved by the amorphous method; the crystallization process of the prepared nanocrystalline alloy was controlled by the growth of the nanocrystalline; the prepared Fe based nanocrystalline alloy was more suitable for the common mode choke core, and can reflect different degrees of magnetic properties under the influence of different annealing temperatures; the prepared Fe based nanocrystalline alloy was better than the coarse-grained alloy. It had higher microhardness and elastic modulus. The solidification sensitivity of this nanocrystalline alloy was completely confirmed by these experimental findings.

electrochemistry