Abstract:The present work investigated the effects of magnetic field annealing on the magnetic properties, mechanical properties and microstructure of the Fe80Si9B11 amorphous alloys. The results show that the soft magnetic properties (SMPs) were obviously improved after the samples were annealed below the crystallization temperature with a 1 T magnetic field. The atom probe tomography (APT) results showed that the magnetic field has little effect on the element distribution of the annealed samples at 653 K. The results of XRD and TEM showed that the 653 K x 0 T sample included a few nanocrystals and an amorphous matrix while the 653 K x 1 T sample still retained an amorphous structure. It is worth noting that a large number of spherical symmetry clusters and a small number of translational symmetry clusters can be observed in the 653 K x 1 T sample. Many translational symmetry clusters, and a few spherical symmetry clusters, can be identified in the 693 K x 1 T sample. Both good soft magnetic properties (SMPs) and acceptable mechanical properties were obtained after the sample was annealed at 653 K. Compared with that of the as-cast sample, the values of maximum magnetic flux intensity (B-m), elastic modulus (E-r) and hardness increased by 13.7%, 36.6% and 9.4%, respectively, while the values of coercivity (H-c) and hysteresis loss (P-u) decreased by 71.5% and 68.2%, respectively. After the sample was annealed at 693 K, the SMPs exhibited a deterioration, and Er and hardness also dropped sharply. Based on the above results, the mechanism of the microstructural change for Fe80Si9B11 amorphous alloys related to the magnetic field annealing conditions was proposed. The relationship between the soft magnetic properties, mechanical properties, and the microstructure of the sample was also discussed. This paper provides a basis for the further improvement the SMPs of the Fe80Si9B11 amorphous ribbons by controlling the microstructure.

Structural and Magnetic Characterization of Fe-Based Amorphous Alloy Prepared by Microwave Annealing Treatment

Effect of Annealing on the Microstructure and Magnetic Properties of Fe-based Nanocomposite Materials

High-temperature Magnetic Properties of Fe-based Nanocrystalline Alloy

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Effect of heat treatment on the microwave electromagnetic properties of flaky Fe-Si-Al magnetic powders

Microwave absorbing mechanism of soft magnetic alloy Fe85Si2Al6Cr7

Evolution from Amorphous to Nanocrystalline and Corresponding Magnetic Properties of Fe-Si-B-Cu-Nb Alloys by Melt Spinning and Spark Plasma Sintering

Influence of Annealing Temperature on Microstructure and Magnetic Properties of FeSiNbCuBP Amorphous Alloys

The Effects of Magnetic Field Annealing on the Magnetic Properties and Microstructure of Fe 80 Si 9 B 11 Amorphous Alloys

Microwave absorbing capability of Fe85Si1Al6Cr8 nanocrystalline flakes

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Microwave absorbing capability of nanocrystalline flakes

Effect of Annealing on the Magnetostatic and Microwave Electromagnetic Properties of Glass-Coated Fe-Rich Microwires

Effects of Annealing on the Microstructure and Magnetic Property of the Mechanically Alloyed FeSiBAlNiM (m=co, Cu, Ag) Amorphous High Entropy Alloys

Atomic level simulation of amorphous/nanocrystalline transition behavior in the Fe based amorphous alloys

Influence of Annealing Process on Soft Magnetic Properties of Fe-B-C-Si-P Amorphous Alloys

Effect of annealing temperature on magnetic properties and corrosion resistance of Fe75.8Si12B8Nb2.6Cu0.6P1 alloy

Magnetic field annealing of FeCo-based amorphous alloys to enhance thermal stability and Curie temperature

Effect of multi-step annealing with different heating rates on magnetic properties of Fe-Si-B-P-Cu nano-crystalline alloy

Modulation of soft magnetic properties of Fe83B10P4C2Cu1 amorphous alloys by V addition and annealing treatment