Revealing the relationship between microstructures, textures, and mechanical behaviors of cold-rolled Al0.1CoCrFeNi high-entropy alloys

Jinxiong Hou,Junwei Qiao,Junhe Lian,Peter K. Liaw

DOI: https://doi.org/10.1016/j.msea.2021.140752

2021-02-01

Abstract:<p>Here we reveal and discuss the relationship among microstructures, textures, and mechanical behaviors of Al_0.1CoCrFeNi high-entropy alloys (HEAs) after cold rolling and annealing. The initially coarsen grains display profuse lamellar-structured slip bands upon cold rolling to 50% reduction with mostly extending vertically to the rolling direction. Meanwhile, cold rolling facilitates the evolutions of Goss ({011} &lt;100&gt;) and Brass ({110} &lt;112&gt;) component textures in the low stacking fault energy (SFE) HEAs accompanying with the formation of deformation twins. Interestingly, the rolling strengthen HEAs exhibit novel anisotropies of yield strength and strain hardening associating more with the direction of the slip lines and twins rather than the rolling-induced preferred orientations, attributing to the easier dislocations glide in between the slip lines and twins than across them. The microstructural characters including dislocation density, slip lines, and twins are quantitatively evaluated, which demonstrates that the dynamic grain refinement contributes much more for the overall strength, compared to the increased dislocation density. A lower strength (370 MPa for yield and 733 MPa for failure) and exceptional ductility (~55%) are achieved in the annealed samples with random grain orientations.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to reveal the relationship between the microstructure, texture, and mechanical properties of Al0.1CoCrFeNi high entropy alloys (HEAs) after cold rolling and annealing treatment. Specifically:

1. **Microstructure Changes**: The study found that after 50% cold rolling, the initially coarse grains exhibited rich lamellar slip bands, which mainly extended along the rolling direction. As the degree of cold rolling increased to 70%, the density of slip bands significantly increased, and the spacing between slip bands became smaller, eventually evolving into shear bands.

2. **Texture Evolution**: Cold rolling promoted the development of Goss ({011} <100>) and Brass ({110} <112>) component textures, accompanied by the formation of deformation twins. These texture changes are related to the low stacking fault energy (SFE).

3. **Mechanical Properties**: The high entropy alloys after cold rolling exhibited new anisotropic yield strength and strain hardening characteristics, which are mainly related to the direction of slip lines and twins, rather than the preferred orientation caused by cold rolling. In annealed samples, random grain orientation led to lower strength (yield strength 370 MPa, fracture strength 733 MPa) and excellent ductility (about 55%).

By quantitatively evaluating microstructural features (such as dislocation density, slip lines, and twins), the study found that dynamic grain refinement contributed much more to the overall strength than the increase in dislocation density. Overall, this study aims to elucidate the complex relationship between the microstructure, texture, and mechanical behavior of high entropy alloys during cold rolling and annealing processes.